Electromigration analysis of solder joints under ac load: A mean time to failure model
نویسندگان
چکیده
Related Articles Electromigration induced fast L10 ordering phase transition in perpendicular FePt films Appl. Phys. Lett. 102, 022411 (2013) Feedback-controlled electromigration for the fabrication of point contacts Appl. Phys. Lett. 102, 023105 (2013) Rapid reversible electromigration of intercalated K ions within individual MoO3 nanobundle J. Appl. Phys. 113, 024311 (2013) Temperature and pressure dependent Mott potentials and their influence on self-limiting oxide film growth Appl. Phys. Lett. 101, 171605 (2012) Electromigration-driven complex dynamics of void surfaces in stressed metallic thin films under a general biaxial mechanical loading J. Appl. Phys. 112, 083523 (2012)
منابع مشابه
Computational damage mechanics of electromigration and thermomigration
Articles you may be interested in Thermomigration and electromigration in Sn58Bi solder joints Electromigration in flip chip solder joints having a thick Cu column bump and a shallow solder interconnect Effect of entropy production on microstructure change in eutectic SnPb flip chip solder joints by thermomigration Appl. Reliability of solder joints under Electromigration (EM) and Thermomigrati...
متن کاملElectromigration in Solder Joints and Solder Lines
Au (0.05 μm) 69.4 μm Electromigration may affect the reliability of flip-chip solder joints. Eutectic solder is a two-phase alloy, so its electromigration behavior is different from that in aluminum or copper interconnects. In addition, a flipchip solder joint has a built-in currentcrowding configuration to enhance electromigration failure. To better understand electromigration in SnPb and lead...
متن کاملDamage mechanics of electromigration and thermomigration in lead-free solder alloys under alternating current: An experimental study
Electromigration and thermomigration reliability of Sn96.5%Ag3.0%Cu0.5 (SAC305 by weight) solder joints under alternating current is studied experimentally with the maximum current density from 2.1 10 A/cm to 1.76 10 A/cm, and frequency from 100 kHz to 4 MHz. During the experiment, hot spots are observed at current crowding corners and the skin layer of solder joints. As a result, highly locali...
متن کاملMean-time-to-failure study of flip chip solder joints on CuÕNi„V...ÕAl thin-film under-bump-metallization
Electromigration of eutectic SnPb flip chip solder joints and their mean-time-to-failure ~MTTF! have been studied in the temperature range of 100 to 140 °C with current densities of 1.9 to 2.75 310 A/cm. In these joints, the under-bump-metallization ~UBM! on the chip side is a multilayer thin film of Al/Ni~V!/Cu, and the metallic bond-pad on the substrate side is a very thick, electroless Ni la...
متن کاملRelieving Hot-Spot Temperature and Current Crowding Effects During Electromigration in Solder Bumps by Using Cu Columns
Solder joints with Cu columns appear to be one of the best structures to resist electromigration. Three-dimensional thermoelectrical analysis was employed to simulate the current density and temperature distributions for eutectic SnPb solder bumps with 0.5, 5, 25, 50, and 100 lm Cu under bump metallization (UBM). It was found that the hot spots and current crowding effects in the solder were re...