High Performance Shape Memory Polyurethane Synthesized with High Molecular Weight Polyol as the Soft Segment

Shape memory polyurethanes (SMPUs) are typically synthesized using polyols of low molecular weight (MW~2,000 g/mol) as it is believed that the high density of cross-links in these low molecular weight polyols are essential for high mechanical strength and good shape memory effect. In this study, polyethylene glycol (PEG-6000) with MW ~6000 g/mol as the soft segment and diisocyanate as the hard segment were used to synthesize SMPUs, and the results were compared with the SMPUs with polycaprolactone PCL-2000. The study revealed that although the PEG-6000-based SMPUs have lower maximum elongations at break (425%) and recovery stresses than those of PCL-based SMPUs, they have much better recovery ratios (up to 98%) and shape fixity (up to 95%), hence better shape memory effect. Furthermore, PEG-based SMPUs showed a much shorter actuation time of <10 s for up to 90% shape recovery compared to typical actuation times of tens of seconds to a few minutes for common SMPUs, demonstrated their great potential for applications in microsystems and other engineering components. OPEN ACCESS Appl. Sci. 2012, 2 536