Characteristics of the Energetic Igniters Through Integrating B/Ti Nano-Multilayers on TaN Film Bridge

The energetic igniters through integrating B/Ti nano-multilayers on tantalum nitride (TaN) ignition bridge are designed and fabricated. The X-ray diffraction (XRD) and temperature coefficient of resistance (TCR) results show that nitrogen content has a great influence on the crystalline structure and TCR. TaN films under nitrogen ratio of 0.99 % exhibit a near-zero TCR value of approximately 10 ppm/°C. The scanning electron microscopy demonstrates that the layered structure of the B/Ti multilayer films is clearly visible with sharp and smooth interfaces. The electrical explosion characteristics employing a capacitor discharge firing set at the optimized charging voltage of 45 V reveal an excellent explosion performance by (B/Ti) n /TaN integration film bridge with small ignition delay time, high explosion temperature, much more bright flash of light, and much large quantities of the ejected product particles than TaN film bridge.