Indium tin oxide exhibiting high poly-crystallinity on oxygen plasma-treated polyethylene terephthalate surface
نویسندگان
چکیده
Low-resistivity indium tin oxide [ITO] film was successfully deposited on oxygen plasma-treated polyethylene terephthalate [PET] surfaces at room temperature. X-ray diffraction [XRD] measurements demonstrated that the film deposited on the PET surface that had not been treated with oxygen plasma had an amorphous structure. In contrast, after the low-power oxygen plasma treatment of the PET surface, the ITO film deposited on the PET surface had a poly-crystalline structure due to interactions between electric dipoles on the PET surface and electric dipoles in the ITO film. The minimum resistivity of the poly-crystalline ITO was about 3.6 times lower than that of the amorphous ITO film. In addition, we found that the resistivity of ITO film is proportional to the intensity of the (400) line in the film's XRD spectra.
منابع مشابه
All-solution-processed PbS quantum dot solar modules.
A rapid increase in power conversion efficiencies in colloidal quantum dot (QD) solar cells has been achieved recently with lead sulphide (PbS) QDs by adapting a heterojunction architecture, which consists of small-area devices associated with a vacuum-deposited buffer layer with metal electrodes. The preparation of QD solar modules by low-cost solution processes is required to further increase...
متن کاملCreating Cellular Micropatterns by Switching Fouling Properties of Electroactive Ito Surfaces
This paper describes a novel approach of forming micropatterned co-cultures using a combination of oxygen plasma ashing and electrochemical removal of poly(ethylene glycol) (PEG) silane from indium tin oxide (ITO) substrates. After assembling a layer of PEG silane on ITO, photolithography and oxygen plasma cleaning were used to form cell-adhesive domains within the non-fouling PEG silane layer....
متن کاملEnhanced Physical Properties Of Indium Tin Oxide Films Grown on Zinc Oxide-Coated Substrates
Structural, electrical and optical properties of indium tin oxide or ITO (In2O3:SnO2) thin films on different substrates are investigated. A 100-nm-thick pre-deposited zinc oxide (ZnO) buffer layer is utilized to simultaneously improve the electrical and optical properties of ITO films. High purity ZnO and ITO layers are deposited with a radio frequency sputtering in argon ambient with plasma p...
متن کاملDevelopment and characterization of a secondary RF plasma-assisted closed-field dual magnetron sputtering system for optical coatings on large-area substrates
An RF-assisted closed-field dual magnetron sputtering system was developed to characterize the plasma and the ionization fraction of sputtered material to provide a suitable system for depositing optical thin films on large-area substrates at low temperatures (<130 ◦C). The ‘prototype’ system consists of dual 76 mm dc magnetrons operated at both balanced and unbalanced (closed-field) configurat...
متن کاملA photo-polymerization resist for UV nanoimprint lithography
A novel liquid photo-polymerization resist was prepared for nanoimprint lithography on transparent flexible plastic substrates. The resist is a mixture of polymethylmethacrylate (PMMA), methylmethacrylate (MMA), methacylic acid (MAA) and two photo-initiators, (2-isopropyl thioxanthone (ITX) and ethyl 4-(dimethylamino)benzoate (EDAB)). The resist can be imprinted at room temperature with a press...
متن کامل