Effects of Al interlayer coating and thermal treatment on electron emission characteristics of carbon nanotubes deposited by electrophoretic method
نویسندگان
چکیده
The effects of aluminum (Al) interlayer coating and thermal post-treatment on the electron emission characteristics of carbon nanotubes (CNTs) were investigated. These CNTs were deposited on conical-shaped tungsten (W) substrates using an electrophoretic method. The Al interlayers were coated on the W substrates via magnetron sputtering prior to the deposition of CNTs. Compared with the as-deposited CNTs, the thermally treated CNTs revealed significantly improved electron emission characteristics, such as the decrease of turn-on electric fields and the increase of emission currents. The observations of Raman spectra confirmed that the improved emission characteristics of the thermally treated CNTs were ascribed to their enhanced crystal qualities. The coating of Al interlayers played a role in enhancing the long-term emission stabilities of the CNTs. The thermally treated CNTs with Al interlayers sustained stable emission currents without any significant degradation even after continuous operation of 20 h. The X-ray photoelectron spectroscopy (XPS) study suggested that the cohesive forces between the CNTs and the underlying substrates were strengthened by the coating of Al interlayers.
منابع مشابه
Synthesis of carbon nano structures on Fe/Cu/AI and Al/Steel by thermal chemical vapour deposition method
Using C2H2, 112 and As gases at 550'C, carbon nanotubes were fabricated on the surfaces of twosubstrates coated by nano thin layers of metal catalysts by DC magnetron sputtering. AYStamless steel andFe/CteAl, by thermal chemical vapor deposition (TCVD) The surface properties of the substrates wereparticularly investigated, and the effect of treatment of the substrates on the CNT's growth is cri...
متن کاملCorrosion Resistance Enhancement of AZ91 Magnesium Alloy Using Ni-P Interlayer and Electrophoretic Deposited 3YSZ Coating
The zirconia stabilized by 3mol % Y2O3 (3YSZ) was applied onto the surface of the magnesium alloy AZ91D using electrophoretic deposition (EPD) from a non- aqueous solution. A Ni-P interlayer between the substrate and YSZ coating was also prepared by electroless plating. Finally, coatings were heat treated in control atmosphere at 400 °C. The preparation, microstructure and corrosion resistance ...
متن کاملElectrophoretic Deposition of Microwave Combustion Synthesized Hydroxyapatite and Its Carbon Nanotube Reinforced Nanocomposite on 316L Stainless Steel
Nanohydroxyapatite-carbon nanotube Nanocomposite (HA-CNT) coatings were deposited via electrophoretic deposition (EPD). Hydroxyapatite was synthesized via microwave combustion method using calcium nitrate and glycing as starting materials. X-ray diffraction (XRD) and Fourier transform infrared spectroscopy (FTIR) revealed that pure hydroxyapatite nanoparticles have been synthesized. AISI 316L s...
متن کاملPreparation of Nanohydroxyapatite-Carbon Nanotube Composite Coatings on 316L Stainless Steel Using Electrophoretic Deposition
Nanohydroxyapatite-carbon nanotube composite coatings were deposited via electrophoretic deposition (EPD). AISI 316L stainless steel and ethanol were used as substrate and dispersing medium, respectively. 5%wt carbon nanotube (CNT) was used as reinforcing phase. Uniform and macrocrack-free coatings were obtained both for hydroxyapatite (HA) and HA-5%wt CNT coatings. Scanning electron micros...
متن کاملEvaluation of the Effect of Ni-Co NPs for the Effective Growth of Carbon Nanotubes by TCVD System
A systematic study was conducted to understand the influences of catalyst combination as Ni-Co NPs on carbon nanotubes (CNTs) grown by Chemical Vapor Deposition (TCVD). The DC-sputtering system was used to prepare Co and Ni-Co thin films on silicon substrate. Ni- Co nanoparticles were used as metal catalyst for growing carbon nanotubes from acetylene (C2H2) gas in 850 ̊ C during 15 min. Carb...
متن کامل