On the mechanisms of the corrosion of weathering steel by SO 2 in laboratory studies: influence of the environmental parameters
نویسنده
چکیده
We report here on the mechanisms underlying the corrosion of weathering steel in accelerated laboratory tests using artificially polluted SO2-atmospheres. The role of corrosion parameters such as the SO2 concentration, the exposure time, the relative humidity and temperature of the environment are discussed in detail. Through the extensive use of Mössbauer spectroscopy in both its transmission and electron detection modes, as well as with the help of other analysis techniques, the characterization of the different corrosion products at the various stages of the corrosion process has been carried out. The results complement the data obtained in field studies and help to understand the mechanisms involved in this complex phenomenon.
منابع مشابه
Quantum chemical studies on adsorption of imidazole derivatives as corrosion inhibitors for mild steel in 3.5 NaCl solution
Adsorption of benzimidazole, 2-methylbenzimidazole and 2-aminobenzimidazole on mild steel in 3.5 NaCl solution was studied using density function theory DFT calculations. In this regard, charge transfer resistance Rct and double layer capacitance Cdl obtained by electrochemical impedance spectroscopy EIS were used to calculate surface coverage and to build prediction models. When prediction mod...
متن کاملElectrochemical and Tribological Behaviour of Oxide Dispersion Strengthened Duplex Stainless Steel in Mine Water Environment
Abstract This work investigated the electrochemical and aqueous tribological behavior of hot pressed 2205 duplex stainless steel (DSS). DSS sintered composites of different volume percent (% vol) of partially stabilized zirconia (PSZ) was developed using powder metallurgy (PM) technique. Electrochemical behaviour was studied at room temperature, using open circuit potential and potentiody...
متن کاملElectrochemical and Theoretical Studies of Adsorption of 1-H-benzotriazole at Stainless Steel in Hydrochloric acid Solution Interface as Corrosion Inhibitors
The influence of the concentration of1-H-benzoteriazolon the corrosion of 316 stainless steel (SS) in chloride acid 1M solutions was studied. The potentiodynamics polarization and scanning electron microscopy (SEM) have been used. The inhibition efficiency increased with an increase in the concentration of1-H-benzoteriazol.The adsorption of1-H-benzoteriazol onto the SS surface occurs accord...
متن کاملStress- Corrosion Crack Initiation of High-strength Pipeline Steel in Near-neutral pH Environments
Stress-corrosion cracking (SCC) tests were conducted in the near-neutral pH standard solution, NS4, and in an actual soil solution, using four-point bending at a high stress ratio and low frequency conditions very similar to those of operational pipelines. Pitting incubation appeared first and then pitting initiated and grew in both solutions although there were many more pits on the specimen t...
متن کاملAn investigation of the corrosive wear of steel balls in grinding of sulphide ores
Ball mills are common grinding equipment in mineral processing industries. Ball wear results from three mechanisms namely impact, abrasion and corrosion. Of these, the corrosion mechanism is the least investigated, due to its chemical-electrochemical nature. Therefore, the aims of this research were to investigate the grinding chemistry influence (slurry pH, solid percentage, water chemistry an...
متن کامل