Structural Transformation of Immiscible Metals Induced by Mechanical Alloying
نویسندگان
چکیده
X-ray absorption fine structure(XAFS) is used to investigate the local structural change of Fe60Cu40 and FegoCu20 with the ball milling time. The XAFS results verify that the solid solution of mechanically alloyed Fe-Cu samples are inhomogeneous. We propose that the bcc to fcc structural transformation of Fe small particles of Fe60Cuq0(160h) is induced by interfacial Cu atoms dissolving in small Fe grain boundary during the mechanical alloying process.
منابع مشابه
Effect of Mechanical Alloying and Sintering on Phase Transformation, Microstructural Evolution, Mechanical Properties and Density of Zr-Cr Alloy
The purpose of present research was production ofZr-based alloy as the nuclear fuel cladding by mechanical alloying (MA) and sintering process. Firstly, Zr and Cr powders were mechanically alloyed to produce the refractory and hard Zr-10 wt% Cr alloy, and then, the powder mixtures were consolidated by press and following sintering at temperature of 800˚C min. The phase evolution, microstructura...
متن کاملElectro-Synthesis of Cu-Nb Nanocomposites; Toward Novel Alloying of Immiscible Bimetals
Immiscible metals due to their inherent specs are insoluble over the steady state. Developing an innovative approach to this issue would be fascinating and challenge the overriding rules. Herein, we proffer the principles of synthesis of Cu-Nb nanocomposites using electrochemical deoxidation route. This method consists of the cathodic electrolysis of the nanoparticles Cu-Nb2O5 through the...
متن کاملStructural and Mechanical Characterization of Austempered Cu - Sn Ductile Iron Alloys
The effect of heat treatment and alloying elements of copper and tin on the microstructure and mechanical properties of austempered ductile cast iron alloys is investigated. The austenitizing temperature of 890°C, the isothermal transformation (austempering) temperatures of 285, 335 and 375°C, and austempering times of 15, 30, 75 and 150 minutes are studied. The alloying elements of copper and ...
متن کاملStructural Characterization and Ordering Transformation of Mechanically Alloyed Nanocrystalline Fe-28Al Powder
The synthesis of nanocrystalline Fe3Al powder by mechanical alloying as well as the structural ordering of the synthesized Fe3Al particles during the subsequent thermal analysis were investigated. Mechanical alloying was performed up to 100 hours using a planetary ball mill apparatus with rotational speed of 300 rpm under argon atmosphere at ambient temperature. The synthesized powders were cha...
متن کاملSynthesis and Characterization of Nanocrystalline Ni3Al Intermetallic during Mechanical Alloying Process
In this research, formation of nanocrystalline Ni3Al intermetallic from Ni and Al elemental powders by mechanical alloying (MA) process and its characterization was investigated. Therefore, the evolutions in microstructure such as phase transformation, oxidation in air and introduction of Fe impurity from milling media after MA were evaluated using XRD, Rietveld refinement, TEM, SEM, EDS and IC...
متن کامل