CuO/ZnO core/shell heterostructure nanowire arrays: synthesis, optical property, and energy application.
نویسندگان
چکیده
Aligned CuO nanowires (NWs) were synthesized by a simple cost-effective oxidation method. They act as cores; high density CuO/ZnO core/shell heterostructure NWs were fabricated by thermal decomposition. Using the core/shell heterostructure NWs as a photoelectrode, a 0.71% photo-to-hydrogen conversion efficiency was obtained from photoelectrochemical water decomposition.
منابع مشابه
Synthesis and characterization of aligned ZnO/BeO core/shell nanocable arrays on glass substrate
By sequential hydrothermal growth of ZnO nanowire arrays and thermal evaporation of Be, large-scale vertically aligned ZnO/BeO core/shell nanocable arrays on glass substrate have been successfully synthesized without further heat treatment. Detailed characterizations on the sample morphologies, compositions, and microstructures were systematically carried out, which results disclose the growth ...
متن کاملControllable Synthesis of Copper Oxide/Carbon Core/Shell Nanowire Arrays and Their Application for Electrochemical Energy Storage
Rational design/fabrication of integrated porous metal oxide arrays is critical for the construction of advanced electrochemical devices. Herein, we report self-supported CuO/C core/shell nanowire arrays prepared by the combination of electro-deposition and chemical vapor deposition methods. CuO/C nanowires with diameters of ~400 nm grow quasi-vertically to the substrates forming three-dimensio...
متن کاملC1jm10762c 9564..9569
Three-dimensional (3D) ZnO–CuO core-shell nanorod arrays have been synthesized by a three-step process on silicon (100) substrates. A hydrothermal method was used to grow 3D ZnO nanorod arrays, followed by deposition of Cu nanofilm using sputtering, which was oxidized subsequently at 400 C to form CuO shell surrounding ZnO nanorod core. The control over oxygen flow and pressure during the Cu na...
متن کاملGrowth and characterization of ZnO/ZnTe core/shell nanowire arrays on transparent conducting oxide glass substrates
We report the growth and characterization of ZnO/ZnTe core/shell nanowire arrays on indium tin oxide. Coating of the ZnTe layer on well-aligned vertical ZnO nanowires has been demonstrated by scanning electron microscope, tunneling electron microscope, X-ray diffraction pattern, photoluminescence, and transmission studies. The ZnO/ZnTe core/shell nanowire arrays were then used as the active lay...
متن کاملOptical properties of crystalline-amorphous core-shell silicon nanowires.
The optical absorption in a nanowire heterostructure consisting of a crystalline silicon core surrounded by a conformal shell of amorphous silicon is studied. We show that they exhibit extremely high absorption of 95% at short wavelengths (λ < 550 nm) and a concomitant very low absorption of down to less than 2% at long wavelengths (λ > 780 nm). These results indicate that our nanowires do not ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 46 36 شماره
صفحات -
تاریخ انتشار 2010