Oxidation and Volatilization of TZM Alloy in Air
نویسندگان
چکیده
منابع مشابه
High Temperature Erosion- Oxidation Behavior of Nickel- Based Alloys Containing Mo in Fluidized Bed Waste Incineration
High-temperature erosion-oxidation behavior of nickel-based alloys containing 0-7 wt.% Mo in fluidized bed waste incineration conditions was studied. A stream of hot condensed air with a flow rate of 25 L/min caused hot silica sand (700 °C) mixed with 0.5 wt.% of chloride salts to hit the specimens for 250 h. By removing the erosive factor, the high-temperature oxidation behavior of the alloys ...
متن کاملHigh Temperature Oxidation Behaviour of Nimonic - 115 Alloy in Presence of Sodium Salts at 850OC
The high temperature oxidation behaviour of Nimonic-115 industrial alloy has been investigated in presence of NaNO3, Na2CO3 and Na2O2 at 850oC in flowing air. The oxidation kinetics and effect of salt deposition for the period of 48 h were studied. The scale morphologies were determined on the basis of X-ray diffraction anal...
متن کاملA study of oxidation behavior of AZ91D alloy with YSZ coating using EIS
Oxidation behavior of AZ91D magnesium alloy with 3YSZ coating and aluminum interlayer was studied in air at 250 °C using electrochemical impedance spectroscopy EIS, scanning electron microscopy SEM, and X-ray diffraction XRD. The oxidation process was carried out in various duration times from 1 to 10 h. A three-electrode electrochemical cell was employed for all the EIS measurements. Also, to ...
متن کاملOxidation Processes and Phase Changes in Metastable Al–Mg Alloys
Oxidation behavior of metastable mechanical alloys in the Al–Mg binary system has been examined in the context of high-energy density materials and combustion applications. Mechanical alloy powders with compositions ranging from Al0.95Mg0.05 to Al0.5Mg0.5, as well as the component metals, were heated at 20 K/min in oxygen. Differential thermal analysis and thermogravimetric analysis showed that...
متن کاملChromium Deposition on Cobalt-Based Alloys by Pack-Cementation and Behaviour of the Coated Alloys in High Temperature Oxidation
Two TaC-strengthened cobalt-based alloys, with compositions Co-10Cr-0.25C-4.4Ta and Co-10Cr-0.5C-8.7Ta (wt.%) underwent Cr-deposition by pack-cementation, followed by heat-treatment to allow Cr diffusing deeper in their sub-surface. Thereafter they were tested for 50 hours at 1200°C in a thermobalance. These alloys were successfully enriched in chromium, with a maximal content on surface of abo...