The role of 1-hydroxyethane –1, 1-diphosphonic acid on corrosion inhibition performance of calcium gluconate in mild steel
نویسندگان
چکیده
The corrosion rate of mild steel in low corrosive tap water in the absence and presence of 1hydroxy ethane-1, 1-diphosphonic acid (HEDP) and calcium gluconate have been evaluated by weight loss, electrochemical polarization and AC impedance measurements. Presence of calcium gluconate considerably enhanced the corrosion inhibition efficiency of the widely used water treatment agent HEDP. At higher concentrations (>50ppm), HEDP was found to be aggressive towards mild steel. But a formulation consisting of 25ppm HEDP and 200ppm calcium gluconate was found to protect mild steel effectively.
منابع مشابه
Acetylacetonate Complexes as New Corrosion Inhibitors in Phosphoric Acid Media: Inhibition and Synergism Study
The corrosion inhibition performance of acetylacetonate complexes of zinc(II), manganese(II), cobalt(II) and copper(II) on the mild steel substrate in 1M H3PO4 was studied using DC polarization. It was seen that the mentioned complexes decreased corrosion rate of mild steel in phosphoric acid media due to the adsorption on metal surface. The potential of mild steel shifted toward more active po...
متن کاملSYNERGISTIC INFLUENCE OF NITRITE ON INHIBITION OF MILD STEEL CORROSION IN CHLORIDE CONTAMINATED ALKALINE SOLUTION
Corrosion behavior of mild steel in chloride contaminated alkaline solution has been studied for the period up to 100days. Saturated Calcium hydroxide solution was used as alkaline solution and 0.5M NaCl solution was used to accelerate mild steel corrosion. The Charge transfer resistance Rct, Current density Icorr and inhibition efficiency values were obtained from tafel polarization and electr...
متن کاملMild steel surface pretreatment using phosphoric acid-inhibitor solution
In this study, a new mild steel surface pretreatment solution is introduced based on phosphoric acid containing a benzimidazole derivative as inhibitor. In this way, three different benzimidazole derivatives namely benzimidazole BI, 2-methyl benzimidazole 2MBI and 2-aminobenzimidazole 2ABI were studied in the 1M H3PO4 using DC and AC electrochemical techniques. Results revealed the better corro...
متن کاملSynergistic Influence of Benzoate Ions on Inhibition of Corrosion of Mild Steel in 0.5m Sulfuric Acid by Benzotriazole
The influence of benzoate anions on the corrosion inhibition effect of benzotriazole (BTA) for mild steel in sulfuric acid has been investigated. The investigation was carried out by electrochemical impedance spectroscopy (EIS) and potentiodynamic polarization techniques. The addition of benzoate ions greatly enhances the inhibition efficiency of BTA in a synergistic manner. This effect has bee...
متن کاملInhibition of Mild Steel Corrosion in Sulfuric Acid Solution by 2-Hydropyrimidine-2-Thione Derivative
The corrosion inhibition potential and efficacy of 2-hydropyrimidine-2-thione derivative on mildsteel in 0.5 M sulfuric acid solution was investigated using electrochemical polarization and FTIRspectroscopic techniques. In addition, docking studies were carried out as theoretical investigationof adsorption inhibitor on iron surface. The results of polarization studies indicate...
متن کامل