Investigation of Low Mole Ratio UF and UMF Resins Aimed at Lowering the Formaldehyde Emission Potential of Wood Composite Boards

نویسندگان

  • An Mao
  • El Barbary Hassan
  • Moon G. Kim
چکیده

Urea-melamine-formaldehyde (UMF) resins with 2.5% and 5.0% melamine levels added at the beginning of the third step of the typical urea-formaldehyde (UF) synthesis procedure were synthesized with an F/(U+M) mole ratio of 1.05 and evaluated as particleboard binders to investigate the positive effects of melamine on the formaldehyde content and physical performance of boards. Resins were tested for storage properties and analyzed by 13 C NMR. Curing catalysts were studied, curing rates were measured, and laboratory particleboards were prepared and tested for formaldehyde contents as well as strength and water-soak test values. The UMF resins resulted in slower curing rates but had adequate board strength values. The formaldehyde content values were within the newly created California emission law (5.2 to 8.0 mg/100 g board). Another objective of this work was to establish the baseline performance of these resins for use in subsequent studies that will aim to reveal the effects of methylene-ether group contents on formaldehyde emissions.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Low Mole Ratio Urea–Melamine–Formaldehyde Resins Entailing Increased Methylene-Ether Group Contents and Their Formaldehyde Emission Potentials of Wood Composite Boards

A previous study of synthesizing low mole ratio urea–formaldehyde (UF) and urea–melamine–formaldehyde (UMF) resins, which included an acidic reaction step at the beginning of the typical resin synthesis procedure to obtain higher uron-type methylene–ether group contents, was repeated with the acidic reaction step extended to a higher viscosity. Compared to previous resins, the synthesized resin...

متن کامل

Low Mole Ratio UF and UMF Resins Entailing Uron-Type Methylene-Ether Groups and their Low Formaldehyde Emission Potentials

The previous study on low mole ratio urea-formaldehyde (UF) and ureamelamine–formaldehyde (UMF) resins synthesized in the typical way as particleboard binders was repeated with the inclusion of a strong acidic reaction step at a mole ratio of 2.7 in the beginning of the resin synthesis procedure. The resulting UF and UMF resins showed longer storageand pot-lives, longer gel times, and the parti...

متن کامل

The Effects of Adding Melamine at Different Resin Synthesis Points of Low Mole Ratio Urea-Melamine- Formaldehyde (UMF) Resins

Low mole ratio urea-melamine-formaldehyde (UMF) resins synthesized with 2.5% and 5.0% melamine levels added at the beginning, middle, and end points of the first alkaline step of the typical urea-formaldehyde (UF) resin synthesis procedure were compared with typical UMF resins synthesized with melamine additions made at the final alkaline step. Various resin analysis, particleboard preparation,...

متن کامل

Development of melamine modified urea formaldehyde resins based on strong acidic pH catalyzed urea formaldehyde polymer

To upgrade the performance of urea-formaldehyde (UF) resin bonded particleboards, melamine modified urea-formaldehyde (MUF) resins based on strong acidic pH catalyzed UF polymers were investigated. The study was conducted in a series of two experiments: 1) formulation of MUF resins based on a UF polymer catalyzed with strong acidic pH and 2) determination of the effects of increased melamine co...

متن کامل

Properties of Particleboard Made from UF with Low-formaldehyde (E1) (TECHNICAL NOTE)

The objective of this study was to manufacture particleboard made from UF with low formaldehyde (E1) for use in indoor environments. The influence of UF in particles on the formaldehyde emission and its mechanical properties were investigated. The experimental results showed that the formaldehyde emission released decreased linearly with consumption UF-low formaldehyde- particle. Formaldehyde e...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2013