Irradiation Induced Localized Amorphization in Mo-Re Alloy Films
نویسندگان
چکیده
To investigate the irradiation properties of Mo-Re alloy of low Re content (atm%: 0% 8:4%), Mo-Re alloy films were irradiated by 200 keV xenon ions at the dose of 5 10 ions/cm. Different irradiation effects were observed on the samples of different Re content. While the sample of pure Mo remained the same after irradiation, obvious localized amorphization phenomenon took place in the sample with Re content of 8.4%. So it is possible that Mo-Re alloy with low Re content might break down for the irradiation induced amorphization process. The formation mechanism of amorphous regions was then discussed by irradiation experiments at ion dose from 1 10 to 5 10 ions/cm, by which the amorphization process developing from lattice damages to amorphous clusters, and finally to amorphous regions, was connected with the increase of irradiation dose step by step. [doi:10.2320/matertrans.M2009306]
منابع مشابه
Compositional Dependent Amorphization in Zr Alloy Films by Means of Ni-Implantation
Ni-implantation has been conducted for sputter deposited Zr alloy films to investigate compositional dependent amorphization behavior in proportion to Ni in Zr alloys. As-deposited Zr and Zr–Cu with thickness of 200 nm shows columnar hcp-Zr and nano-crystalline hcp-Zr(Cu), respectively. Implantation of 150 keV Niþ with the amount of 1 10 ions/cm induces amorphization of Zr and Zr(Cu) with 100 n...
متن کاملRadiation-induced amorphization of crystalline ice
We study radiation-induced amorphization of crystalline ice, analyzing the results of three decades of experiments with a variety of projectiles, irradiation energy, and ice temperature, finding a similar trend of increasing resistance of amorphization with temperature and inconsistencies in results from different laboratories. We discuss the temperature dependence of amorphization in terms of ...
متن کاملMechanical properties and microstructural change of W–Y2O3 alloy under helium irradiation
A wet-chemical method combined with spark plasma sintering was used to prepare a W-Y2O3 alloy. High-temperature tensile tests and nano-indentation microhardness tests were used to characterize the mechanical properties of the alloy. After He-ion irradiation, fuzz and He bubbles were observed on the irradiated surface. The irradiation embrittlement was reflected by the crack indentations formed ...
متن کاملControllable crystal growth and fast reversible crystallization-to-amorphization in Sb2Te-TiO2 films
The structure evolution and crystallization processes of Sb2Te-TiO2 films have been investigated. The Sb2Te-rich nanocrystals, surrounded by TiO2 amorphous phases, are observed in the annealed Sb2Te-TiO2 composite films. The segregated domains exhibit obvious chalcogenide/TiOx interfaces, which elevate crystallization temperature, impede the grain growth and increase crystalline resistance. Com...
متن کاملIon-induced grain growth in multilayer and coevaporated metal alloy thin films
Irradiation experiments were conducted on multilayer (ML) and coevaporated (CO) thin films in order to examine the role that the heat-of-mixing (AH,,,,,) has in ion-induced gram growth. Room-temperature irradiations using 1.7 MeV Xe were performed in the High Voltage Electron Microscope at Argonne National Laboratory. The alloys studied (Pt-Ti, Pt-V, Pt-Ni, Au-Co and Ni-Al) spanned a large rang...