Effects of Nitrogen and Tensile Direction on Stress Corrosion Cracking Susceptibility of Ni-Free FeCrMnC-Based Duplex Stainless Steels
نویسندگان
چکیده
Stress corrosion cracking (SCC) behavior of Ni-free duplex stainless steels containing N and C (Febalance-19Cr-8Mn-0.25C-(0.03, 0.21)N, in wt %) was investigated by using a slow strain rate test (SSRT) in air and aqueous NaCl solution with different tensile directions, including parallel (longitudinal) and perpendicular (transverse) to the rolling direction. It was found that alloying N was effective in increasing the resistance to SCC, while it was higher along the longitudinal direction than the transverse direction. The SCC susceptibility of the two alloys was assessed based on the electrochemical resistance to pitting corrosion, the corrosion morphology, and the fractographic analysis.
منابع مشابه
An Investigation on Corrosion and Stress Corrosion Cracking initiation of a Ferritic Stainless Steel in a Tertiary Amine Solution
The present study focused on stress corrosion cracking (SCC) and corrosion behavior of ferritic stainless steel (grade 430) in activated methyl diethanolamine (aMDEA) solution, which is classified as a tertiary amine. In this regard, cyclic polarization and U-bend tests were performed in CO2 loaded aMDEA with different concentrations at 25 and 70 °C to observe corrosion behavior and ...
متن کاملDynamic Strain Ageing and Eac of Deformed Nitrogen-alloyed Aisi 316 Stainless Steels
Intergranular stress corrosion cracking has occurred in BWR environments in non-sensitised, cold-worked austenitic stainless steel materials. The affecting parameters are so far not fully known, but deformation mechanisms may be decisive. The effect of cold deformation and nitrogen content on the deformation behaviour of austenitic stainless steels was investigated. The materials were austeniti...
متن کاملSCC of 2304 Duplex Stainless Steel—Microstructure, Residual Stress and Surface Grinding Effects
The influence of surface grinding and microstructure on chloride induced stress corrosion cracking (SCC) behavior of 2304 duplex stainless steel has been investigated. Grinding operations were performed both parallel and perpendicular to the rolling direction of the material. SCC tests were conducted in boiling magnesium chloride according to ASTM G36; specimens were exposed both without extern...
متن کامل2686: Investigation of Stress Corrosion Cracking Susceptibility of High Strength Stainless Steels for Use as Strand Material in Prestressed Concrete Construction in a Marine Environment
Stainless steel reinforcing has an elevated chloride threshold and is an attractive alternative for prestressed concrete applications. However, due to the high strength requirements for prestressing strands, concern exists about the possibility of stress corrosion cracking (SCC). This investigation screened for potential SCC development three candidate high strength alloys for use as prestresse...
متن کاملStudy of the Corrosion Resistance of Austenitic Stainless Steels during Conversion of Waste to Biofuel
The paper deals with the corrosion behavior of stainless steels as candidate materials for biofuel production plants by liquefaction process of the sorted organic fraction of municipal solid waste. Corrosion tests were carried out on AISI 316L and AISI 304L stainless steels at 250 °C in a batch reactor during conversion of raw material to bio-oil (biofuel precursor), by exposing specimens eithe...
متن کامل