Structure, scratch resistance and corrosion performance of nickel doped diamond-like carbon thin films

نویسندگان

  • N. W. Khun
  • E. Liu
  • G. C. Yang
چکیده

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Investigation of structure, adhesion strength, wear performance and corrosion behavior of platinum/ruthenium/nitrogen doped diamond-like carbon thin films with respect to film thickness

In this study, the corrosion performance of platinum/ruthenium/nitrogen doped diamond-like carbon (PtRuN-DLC) thin films deposited on p-Si substrates using a DCmagnetron sputtering deposition system in a 0.1M NaCl solution was investigated using potentiodynamic polarization test in terms of film thickness. Theeffect of thefilmthickness on the chemical composition, bonding structure, surfacemorp...

متن کامل

Corrosion behavior of aluminum doped diamond-like carbon thin films in NaCl aqueous solution.

Aluminum doped diamond-like carbon (DLC:Al) thin films were deposited on n-Si(100) substrates by co-sputtering a graphite target under a fixed DC power (650 W) and an aluminum target under varying DC power (10-90 W) at room temperature. The structure, adhesion strength and surface morphology of the DLC:Al films were characterized by X-ray photoelectron spectroscopy (XPS), micro-scratch testing ...

متن کامل

Structure, adhesive strength and electrochemical performance of nitrogen doped diamond-like carbon thin films deposited via DC magnetron sputtering.

Nitrogen doped diamond-like carbon (DLC:N) thin films were deposited on p-Si (100) substrates by DC magnetron sputtering with different nitrogen flow rates at a substrate temperature of about 100 degrees C. The chemical bonding structure of the films was characterized by X-ray photoelectron spectroscopy (XPS) and micro-Raman spectroscopy. The adhesive strength and surface morphology of the film...

متن کامل

Nitrogen-Induced Degradation of Corrosion Resistance of Platinum/Ruthenium/Nitrogen-Doped Diamond-like Carbon Thin Films

An influence of nitrogen incorporation on the chemical composition, bonding structure, surface morphology and activity, adhesion strength, and corrosion resistance of platinum/ruthenium/nitrogen-doped diamond-like carbon PtRuN-DLC thin films deposited on conductive p-Si 100 substrates using dc magnetron sputtering deposition was investigated using X-ray photoelectron spectroscopy, micro-Raman s...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2010