Nucleation mechanisms and the elimination of misfit dislocations at mismatched interfaces
نویسندگان
چکیده
To investigate the effect of growth area on interface dislocation density in strained-layer epitaxy, we have fabricated 2-.um-high mesas of varying lateral dimensions and geometry in (001) GaAs substrates with dislocation densities of 1.5 X 10\ 10, and 10 cm-2 • 3500-, 7000-, and 8250-A-thick Ino (J5 Gao 95 As layers, corresponding to 5, to, and 11 times the experimental critical layer thickness as measured for large-area samples, were then deposited by molecularbeam epitaxy. For the 3500-A layers, the linear interface dislocation density, defined as the inverse of the average dislocation spacing, was reduced from greater than 5000 to less than 800 em I for mesas as large as 100 pm. A pronounced difference in the linear interface dislocation densities along the two interface (110) directions indicates that a dislocations nucleate about twice as much as /3 dislocations. For samples grown on the highest dislocation density substrates, the linear interface-dislocation density was found to vary linearly with mesa width and to extrapolate to a zero linear interface-dislocation density for a mesa width of zero. This behavior excludes dislocation multiplication or the nucleation of surface half"loops as operative nucleation sources for misfit dislocations in these layers. Only nucleation sources that scale with area (termed fixed sources) are active. In specimens with lower substrate dislocation densities, the density of interface dislocations still varies linearly with mesa size, but the slope becomes independent of substrate dislocation density, indicating that surface inhomogeneities now act as the dominant source for misfit dislocations. Thus, in 3500-A-thick overlayers, substrate dislocations and substrate inhomogeneities are the active fixed nucleation sources. Since only fixed nucleation sources are active, a single strained layer wiH dramatically reduce the threading dislocation density in the epilayer. For the 7ooo-A layers, we observe a superlinear increase in linear interface-dislocation density with mesa size for mesas greater than 200,um, indicating that dislocation mUltiplication occurs in large mesas. For mesas less than 200 pm in width, linear interface-dislocation density decreases linearly with mesa size, but extrapolates to a nonzero linear interface-dislocation density for a mesa size of zero. This nonzero extrapolation suggests an additional active source which generates a dislocation density that cannot be decreased to zero by decreasing the mesa size. Cathodoluminescence eeL) images using radiative recombination indicate that the additional source is nucleation from the mesa edges. Despite a doubling in epilayer thickness from 3500 to 7000 A, the linear interface-dislocation density for mesas 100 [tm in width is stm very low, approximately 1500 cm --l. The 8250"A layers possess interface-dislocation densities too high to be accurately determined with CL. However, increases in CL intensity as mesa width is reduced indicate that the interface-dislocation density is decreasing and that growth on small areas produces higherquality layers than growth on large areas. OUf investigations show that different sources fOf misfit dislocations become active at different epHayer strain levels. The critical thickness depends on which type of nucleation source becomes activated first; therefore, different critical thicknesses can be observed depending on which kind of source is present in a specimen.
منابع مشابه
Relaxation Mechanisms, Structure and Properties of Semi-Coherent Interfaces
In this work, using the Cu–Ni (111) semi-coherent interface as a model system, we combine atomistic simulations and defect theory to reveal the relaxation mechanisms, structure, and properties of semi-coherent interfaces. By calculating the generalized stacking fault energy (GSFE) profile of the interface, two stable structures and a high-energy structure are located. During the relaxation, the...
متن کاملDislocation Formation during Vapor Deposition of Epitaxial Multilayers
A molecular dynamics method has been used to study the formation of dislocations during the vapor deposition of NiFe/Au/NiFe/Au and CoFe/NiFe/CoFe/Cu multilayers. We observed the direct nucleation of misfit dislocations (with zero critical thickness) at (111) interfaces in the NiFe/Au/NiFe/Au system. Both the dislocation configuration and density observed in the simulations were similar to thos...
متن کاملStress relaxation and misfit dislocation nucleation in the growth of misfitting films: A molecular dynamics simulation study
The low-temperature growth and relaxation of misfitting films are analyzed on the basis of two-dimensional molecular dynamics simulations using Lennard–Jones potentials. The temporal evolution of the surface morphology and the mechanisms for misfit dislocation nucleation and stress relaxation are monitored. Pseudomorphic film growth is observed up to a critical thickness. In some cases, the for...
متن کاملAtomistic simulation study of misfit strain relaxation mechanisms in heteroepitaxial islands
The mechanisms of the misfit strain relaxation in heteroepitaxial islands are investigated in twodimensional molecular dynamics simulations. Stress distributions are analyzed for coherent and dislocated islands. Thermally-activated nucleation of misfit dislocations upon annealing at an elevated temperature and their motion from the edges of the islands towards the positions corresponding to the...
متن کاملMisfit Dislocations in Epitaxial Heterostructures: Mechanisms of Generation and Multiplication
In this paper, the regularities of dislocation pattern formation in single layer heterostructures with low lattice mismatch (f < 1%) are reviewed. The main attention is focused on the recently suggested mechanisms of dislocation nucleation and multiplication. An evolution of dislocation pattern from regular flat misfit dislocation network to the dense three-dimensional one was found to proceed ...
متن کامل