The microwave power handling of a FIB-generated weak link in a YBCO film

نویسندگان

  • A Cowie
  • M W Denhoff
چکیده

We have measured the power dependent microwave properties of a weak link in a YBa2Cu3O7−δ thin film formed by writing a line of damage using a focused ion beam. The measurement was made using a parallel plate resonator at 5.5 GHz with the weak link written across the width of one of the plates. The ion induced damage was characterized using a TRIM computer simulation and the dc properties of similar weak links was measured. Using a 200 eV Si ion dose of 2× 1013 cm−2, the Tc of the damaged region was reduced by 5.5 K and the normal resistivity was doubled. Surprisingly, the microwave measurements did not show any Josephson junction characteristics. Rather, the ion damaged region exhibited a greatly increased microwave resistivity that was constant as a function of microwave power up to rf fields of 20 mT at 21 K.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Microwave Frequency Power Dependence in High - Tc Thin Films , Grain Boundaries

A comprehensive study of the dc and rf electrodynamic properties of YBa 2 Cu 307-, (YBCO) thin films, grain boundaries and Josephson junctions (JJ) is presented. The surface impedance Z, = R, + iX, of YBCO thin films is shown to have a dependence on rf current, which leads to nonlinear power losses at levels of rf power that are relevant for device applications. To understand the loss mechanism...

متن کامل

Comparison of Power Dependence of Microwave Surface Resistance of Unpatterned and Patterned YBCO Thin Film

The effect of the patterning process on the nonlinearity of the microwave surface resistance RS of YBCO thin films is investigated. With the use of a sapphire dielectric resonator and a stripline resonator, the microwave RS of YBCO thin films was measured before and after the patterning process, as a function of temperature and the rf peak magnetic field in the film. The microwave loss was also...

متن کامل

YBa2Cu307./j-Based, Edge-Geometry SNS Josephson Junctions with Low-resistivity PrBa2Cu307-~ Barriers

We investigated the properties of all-high-Tc edge-geometry Josephson weak links using superconducting YBa2Cu307+ (YBCO) electrodes and PrBa2Cu307-~ (PBCO) normal-metal layers. The fabrication of the weak-links involved first ionmilling the base YBCO film using a MgO mask to form the edge and then depositing PBCO and YBCO layers in situ by pulsed-laser deposition. The optimum PBCO films had res...

متن کامل

Microwave Current Imaging in Passive HTS Components by Low-Temperature Laser Scanning Microscopy (LTLSM)

We have used the Low-Temperature Laser Scanning Microscope (LTLSM) technique for a spatially resolved investigation of the microwave transport properties, nonlinearities, and material inhomogeneities in an operating coplanar waveguide YBa2Cu3O7−δ (YBCO) microwave resonator on a LaAlO3 (LAO) substrate. The influence of twin-domain blocks, in-plane rotated grains, and micro-cracks in the YBCO fil...

متن کامل

RF Power Properties of YBCO-Film/LAO Microstrip Disk Resonators for 4 GHz Band

This paper presents RF power properties of YBCO films on LaAlO3 substrate examined using microstrip disk shape-patterned resonators for around 4 GHz. Characterization of the YBCO films for the resonators was carried out. For input-output power measurement, the resonators with the condition of strong I/O couplings were designed and fabricated. The RF power properties of the resonators at cryogen...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 1999