Effect of Additives on Melting Point and Viscosity of RH Refining Slag
نویسندگان
چکیده
To get suitable ladle slag which can avoid slag sticking onto the RH immersion tube during RH refining process of IF steel, the effect of composition on melting point and viscosity of RH refining ladle slag was studied by different additives which is based on CaO. The results of melting point and viscosity testing experiments indicates that, the melting point and viscosity of RH refining ladle slag would decrease effectively with the add of experimental additives. During RH refining process of IF steel, adjusting the basicity to 4~5, and the content of Al2O3 to 14%~15% by adding additives, it can avoid slag sticking onto the RH immersion tube efficiently, for the reason that the melting point of ladle slag is about 1280 °C, and the viscosity is only 0.65 Pa·s.
منابع مشابه
J. JACKOWSKI*, M. SUCHORA-KOZAKIEWICZ*,# Assessment of usAbIlIty of molten sAlt mIxtures In metAllurgy of AlumInum Alloys And recyclIng of composIte mAterIAls bAsed on the mAtrIx of Al Alloys
Two liquid phases: molton metal (or alloy) and slag occur in most metallurgical systems. The slag occurring at the surface of the metal bath not only protects it against negative atmospheric effects but also enables to make many treatments necessary to achieve good quality of the material designed for shaping the casted products. In the conditions of fully controlled process (e.g. melting or re...
متن کاملThe Effect of Slag Types and Melting Rate on Electro-Slag Remelting (ESR) Processing
In this research, the influence of chemical composition of slags and the melting rate on the impurity of commercial grade iron in ESR processing has been investigated.The chemical composition and microstructure studies were evaluated, using spectrophotometer,OMand EDX analyses attached to SEM.The results show that ESR process has successfully reduced the amount and size of inclusions. In some c...
متن کاملInvestigations of Calcium Aluminate Slag Penetration to MgO Monolithic Refractories in Steelmaking Process
In this study, slag penetration into a magnesia refractory monolithic was investigated by the crucible test method. A synthetic calcium aluminate slag system has been used to study commercial magnesia mix refractory for 1, 2, 3, 4, 5 and 6 hours at 1450°C and 1600°C. It has been shown that the penetration rate is controlled by a diffusion mechanism at 1450°C. In this case, capillaries are the ...
متن کاملThe Effect of Nano-Additives on the Hydration Resistance of Materials Synthesized From the MgO-CaO System (RESEARCH NOTE)
In this study, the effect of variety of Nano- additives doping on the hydration resistance of the MgO-CaO system was investigated. Samples were prepared from calcined dolomite and magnesite. Nano-additives that contained cations with various valences (trivalent and tetravalent) used as a dopant. The bulk density, apparent porosity and hydration resitance were studied and evaluated. Also, phase...
متن کاملThe influence of TiO2 and Na2CO3 on the viscosity and crystallization behavior of mold powders
Mold powders are fluxing agents used as raw materials in the steel industry, which play very important role in processing stability and final surface quality of a product. Surface quality depends particularly on the viscosity and the heat transfer of infiltrated mold flux between the mold wall and the solidified steel shell. Heat flux across the interfacial gap depends on thermal properties of ...
متن کامل