Comparative study of hydroxyapatite coatings obtained by Sol-Gel and electrophoresis on titanium sheets
نویسندگان
چکیده
A comparative study of two coating methods on titanium (Ti) substrates, sol-gel and electrophoresis processes, was performed. Before coating, two different surface treatments were employed. The hydroxyapatite (HA) powder were characterized by infrared spectroscopy (FTIR) and X-ray diffraction (XRD) while coated samples were examined by using scanning electron microscopy (SEM) with energy dispersive spectroscopy (EDS). Both techniques seem to be suitable to coat Ti. A previous surface treatment on metallic titanium seems to be fundamental to enhance coat uniformity and adhesion that was estimated by the adhesive tape test. The decrease in calcination temperature did not affect the coating adhesion.
منابع مشابه
Deposition of Nano-Crystalline Fluor-hydroxyapatite Coatings on Titanium Substrates via Sol-Gel Method
In this investigation, fluor-hydroxyapatite (FHA) film was deposited on a titanium substrate by sol-gel method. Triethyl phosphite, ammonium fluoride and calcium nitrate in ethanol solutions were used respectively as P, F and Ca precursors. Typical apatite structures were obtained for all coatings after dipping and subsequent heat treatment at 550, 700 and 800 ºC, the coating layers were ...
متن کاملSol-Gel Derived Hydroxyapatite, Fluorhydroxyapatite and Fluorapatite Coatings for Titanium Implants
متن کامل
Sol-Gel Derived Titania Coating on Titanium Substrate
The synthesis of titania via sol-gel method has been widely studied. In the present work, titania was deposited onto a titanium substrat...
متن کاملSol-Gel-Derived Hydroxyapatite-Carbon Nanotube/Titania Coatings on Titanium Substrates
In this paper, hydroxyapatite-carbon nanotube/titania (HA-CNT/TiO(2)) double layer coatings were successfully developed on titanium (Ti) substrates intended for biomedical applications. A TiO(2) coating was firstly developed by anodization to improve bonding between HA and Ti, and then the layer of HA and CNTs was coated on the surface by the sol-gel process to improve the biocompatibility and ...
متن کاملInitial responses of human osteoblasts to sol-gel modified titanium with hydroxyapatite and titania composition.
Sol-gel thin films of hydroxyapatite (HA) and titania (TiO(2)) have received a great deal of attention in the area of bioactive surface modification of titanium (Ti) implants. Sol-gel coatings were developed on Ti substrates of pure HA and TiO(2) and two composite forms, HA+10% TiO(2) and HA+20% TiO(2), and the biological properties of the coatings were evaluated. All the coating layers exhibit...
متن کامل