Effect of Fly-Ash Cenospheres on Properties of Clay-Ceramic Syntactic Foams
نویسندگان
چکیده
A low-density clay ceramic syntactic foam (CSF) composite material was successfully synthesized from illitic clay added by fly ash cenospheres (CS) using the semi-dry formation method. The content of CS varied in the range of 10, 30, 50 and 60 vol %. Furthermore, reference samples without cenospheres were produced for property comparison. The materials comprising different amount of the additives were fired at temperatures of 600, 950, 1000, 1050, 1100, 1150 and 1200 °C. Firing times were kept constant at 30 min. Processing characteristics of the materials were evaluated in terms of density achieved and shrinkage observed as functions of both the CS content and the sintering temperature. The compressive strength and water uptake were determined as application-oriented properties. Except for the reference and the low CS level samples, the materials show an increase in strength with the increase in firing temperature, and a decrease of mechanical reliability with a decrease in density, which is typical for porous materials. Exceptions are the samples with no or low (10 vol %) content of cenospheres. In this case, the maximum strength is obtained at an intermediate sintering temperature of 1100 °C. At a low density (1.10 and 1.25 g/cm³), the highest levels of strength are obtained after sintering at 1200 °C. For nominal porosity levels of 50 and 60 vol %, 41 and 26 MPa peak stresses, respectively, are recorded under compressive load.
منابع مشابه
Magnesium Matrix Composite Foams—Density, Mechanical Properties, and Applications
Potential of widespread industrial applications of magnesium has been realized in recent years. A variety of magnesium alloy matrix composites are now being studied for mechanical properties. Since magnesium is the lightest structural metal, it can replace aluminum in existing applications for further weight savings. This review presents an overview of hollow particle filled magnesium matrix sy...
متن کاملStructure and Compressive Properties of Invar-Cenosphere Syntactic Foams
The present study investigates the mechanical performance of syntactic foams produced by means of the metal powder injection molding process having an Invar (FeNi36) matrix and including cenospheres as hollow particles at weight fractions (wt.%) of 5 and 10, respectively, corresponding to approximately 41.6 and 60.0 vol.% in relation to the metal content and at 0.6 g/cm³ hollow particle density...
متن کاملData characterizing tensile behavior of cenosphere/HDPE syntactic foam
The data set presented is related to the tensile behavior of cenosphere reinforced high density polyethylene syntactic foam composites "Processing of cenosphere/HDPE syntactic foams using an industrial scale polymer injection molding machine" (Bharath et al., 2016) [1]. The focus of the work is on determining the feasibility of using an industrial scale polymer injection molding (PIM) machine f...
متن کاملNew Products from Coal Combustion Ash: Selective Extraction of Particles with Density < 2
Spherical and hollow fly ash particles having density < 1g/cm are known as cenospheres. Their concentration in coal combustion ash is typically << 1%; as a consequence, their value is relatively high (~$0.70/kg). However, cenospheres are really particles containing gas bubbles independent of their density. Hence, cenosphere densities can vary between 0.6 g/cm to near or greater than 2.0 g/cm. T...
متن کاملEffect of carbon black and fly ash co-fillers content on mechanical and thermal behaviors of styrene butadiene rubber compounds
Fly ash (FA) is produced as a waste byproduct during the burning process of coal in thermal power plants whose cost is primarily associated to cleaning and transportation. It possesses mechanical properties on account of its constituents like silica and alumina. The use of FA as filler in styrene butadiene rubber (SBR) was of researchers’ interest to reinforce and/or to reduce product cost. In ...