Photoinitiated nitric oxide-releasing tertiary S-nitrosothiol-modified xerogels.
نویسندگان
چکیده
The synthesis of a tertiary thiol-bearing silane precursor (i.e., N-acetyl penicillamine propyltrimethoxysilane or NAPTMS) to enable enhanced NO storage stability at physiological temperature is described. The novel silane was co-condensed with alkoxy- or alkylalkoxysilanes under varied synthetic parameters (e.g., water to silane ratio, catalyst and solvent concentrations, and reaction time) to evaluate systematically the formation of stable xerogel films. The resulting xerogels were subsequently nitrosated to yield tertiary RSNO-modified coatings. Total NO storage ranged from 0.87 to 1.78 μmol cm(-2) depending on the NAPTMS concentration and xerogel coating thickness. Steric hindrance near the nitroso functionality necessitated the use of photolysis to liberate NO. The average NO flux for irradiated xerogels (20% NAPTMS balance TEOS xerogel film cast using 30 μL) in physiological buffer at 37 °C was ∼23 pmol cm(-2) s(-1). The biomedical utility of the photoinitiated NO-releasing films was illustrated by their ability to both reduce Pseudomonas aeruginosa adhesion by ∼90% relative to control interfaces and eradicate the adhered bacteria.
منابع مشابه
Synthesis of Nitric Oxide-Releasing Polyurethanes with S-Nitrosothiol-Containing Hard and Soft Segments.
Nitric oxide (NO)-releasing polyurethanes capable of releasing up to 0.20 μmol NO cm(-2) were synthesized by incorporating active S-nitrosothiol functionalities into hard and soft segment domains using thiol group protection and post-polymerization modifications, respectively. The nitrosothiol position within the hard and soft segment domains of the polyurethanes impacted both the total NO rele...
متن کاملAntimicrobial Activity of Nitric Oxide-Releasing Ti-6Al-4V Metal Oxide
Titanium and titanium alloy materials are commonly used in joint replacements, due to the high strength of the materials. Pathogenic microorganisms can easily adhere to the surface of the metal implant, leading to an increased potential for implant failure. The surface of a titanium-aluminum-vanadium (Ti-6Al-4V) metal oxide implant material was functionalized to deliver an small antibacterial m...
متن کاملThe preparation and characterization of nitric oxide releasing silicone rubber materials impregnated with S-nitroso-tert-dodecyl mercaptan.
Recently, considerable research efforts have focused on increasing the biocompatibility a nd bactericidal activity of biomedical polymeric devices (e.g., catheters, etc.) through incorporation of nitric oxide (NO) releasing molecules. NO is an important endogenous molecule that is well known for enhancing blood flow via its vasodilatory activity, but it also exhibits potent antithrombotic and a...
متن کاملSol-gel derived nitric oxide-releasing oxygen sensors.
An amperometric sol-gel derived sensor that both releases nitric oxide (NO) and measures physiologically relevant concentrations of oxygen (PO2) is described. The sensor consists of a platinum electrode coated with an aminosilane/ethyltrimethoxysilane hybrid xerogel film. Hydrophilic polyurethane (HPU) is doped into the hybrid film to reduce sensor hydration time and increase oxygen permeabilit...
متن کاملSynthesis, characterization, and controlled nitric oxide release from S-nitrosothiol-derivatized fumed silica polymer filler particles.
A new type of nitric oxide (NO)-releasing material is described that utilizes S-nitrosothiols anchored to tiny fumed silica (FS) particles as the NO donor system. The synthetic procedures suitable for tethering three different thiol species (cysteine, N-acetylcysteine, and N-acetylpenicillamine) to the surface of FS polymer filler particles are detailed. The thiol-derivatized particles are conv...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- ACS applied materials & interfaces
دوره 4 2 شماره
صفحات -
تاریخ انتشار 2012