- 1 - Spin glass behavior in an interacting γ - Fe 2 O 3 nanoparticle system
نویسندگان
چکیده
In this paper we investigate the superspin glass behavior of a concentrated assembly of interacting maghemite nanoparticles and compare it to that of canonical atomic spin glass systems. ac versus temperature and frequency measurements show evidence of a superspin glass transition taking place at low temperature. In order to fully characterize the superspin glass phase, the aging behavior of both the thermo-remanent magnetization (TRM) and ac susceptibility has been investigated. It is shown that the scaling laws obeyed by superspin glasses and atomic spin glasses are essentially the same, after subtraction of a superparamagnetic contribution from the superspin glass response functions. Finally, we discuss a possible origin of this superparamagnetic contribution in terms of dilute spin glass models.
منابع مشابه
Structural and magnetic characterization of self-assembled iron oxide nanoparticle arrays.
We report about a combined structural and magnetometric characterization of self-assembled magnetic nanoparticle arrays. Monodisperse iron oxide nanoparticles with a diameter of 20 nm were synthesized by thermal decomposition. The nanoparticle suspension was spin-coated on Si substrates to achieve self-organized arrays of particles and subsequently annealed at various conditions. The samples we...
متن کاملMagnetic coupling mechanisms in particle/thin film composite systems
Magnetic γ-Fe(2)O(3) nanoparticles with a mean diameter of 20 nm and size distribution of 7% were chemically synthesized and spin-coated on top of a Si-substrate. As a result, the particles self-assembled into a monolayer with hexagonal close-packed order. Subsequently, the nanoparticle array was coated with a Co layer of 20 nm thickness. The magnetic properties of this composite nanoparticle/t...
متن کاملFragility of the spin-glass-like collective state to a magnetic field in an interacting Fe- C nanoparticle system
متن کامل
Massively ordered microstructures composed of magnetic nanoparticles.
Magnetic γ-Fe(2)O(3) nanoparticle toluene solution was placed in a restricted, axially symmetric geometry composed of a spherical lens on a Si substrate (i.e., sphere-on-Si geometry), forming a capillary-held solution. The solvent evaporation led to the self-assembly of γ- Fe(2)O(3) nanoparticles into hundreds of spatially well-ordered, gradient concentric 'coffee rings'. The rings were two nan...
متن کاملFe2+ Supported on Hydroxyapatite-core-shell-γ-Fe2O3 Nanoparticles as an Inexpensive and Magnetically-recoverable Catalyst for Rapid Synthesis of Benzimidazoles and Benzoxazole Derivatives
A simple and facile method for the preparation ofFe2+ supported on hydroxyapatite-core-shell-γ-Fe2O3 nanoparticles (γ-Fe2O3@HAp-Fe2+ NPs) as an environmentally friendly and recyclable green catalyst is described and used for the one-pot synthesis of benzimidazoles and benzoxazole derivatives via reactions between aromatic aldehyd...
متن کامل