Effects of Complex Flame Retardant on the Thermal Decomposition of Natural Fiber
نویسندگان
چکیده
Natural fiber is a renewable resource characterized by its low cost and environmental friendliness. However, flame retardant properties are one of the biggest limitations for the preparation of composite materials that need to be improved. In this work, a novel complex flame retardant consisting of aluminum hydroxide (ALH) and decabromine diphenyl oxide (PBDE) was proposed to inhibit the thermal decomposition. Flameretarding paper was made from softwood pulp and complex flame retardant. The thermal properties of the flame retardants were studied using thermogravimetric analysis (TGA). The mechanical properties of paper treated at different temperatures were tested, while the surface characteristics of natural fiber were detected by a scanning electron microscope (SEM) and atomic force microscope (AFM); their specific surface areas were also measured. The optimum value of aluminum hydroxide to decabromine diphenyl oxide was 3 to 1, added at 70% based on dried natural fiber. It also had good flame retardant performance and mechanical properties at 200 °C for 5 min; meanwhile, the tensile index of the handsheet was 82.5 Nm/g, and the specific surface area was 0.414 m2/g.
منابع مشابه
A Fast Method for Synthesis Magnesium Hydroxide Nanoparticles, Thermal Stable and Flame Retardant Poly vinyl alcohol Nanocomposite
Magnesium hydroxide nanostructures as an effective flame retardant were synthesized by a facile and rapid microwave reaction. The effect of different surfactants such as cationic, anionic and polymeric on the morphology of magnesium hydroxide nanostructures was investigated. Nanostructures were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform in...
متن کاملHydrothermal Synthesis of Nickel Hydroxide Nanostructures and Flame Retardant Poly Vinyl Alcohol and Cellulose Acetate Nanocomposites
Nickel hydroxide nanostructures were synthesized by a hydrothermal reaction. The effect of different precursors and surfactants on the morphology of nickel hydroxide nanostructures was investigated. Nanostructures were characterized by X-ray diffraction, energy dispersive X-ray spectroscopy, scanning electron microscopy and Fourier transform infrared spectroscopy. The influence of Ni(OH)2 nano...
متن کاملPerformance of Flame Retardant Wool Fabric Grafted with Vinyl Phosphate
In this paper, a flame retardant dimethyl-2-(methacryloyloxyethyl) phosphate (DMMEP) was applied to wool fabrics by the graft copolymerization technique initiated with potassium persulfate (KPS) in water media. FTIR and SEM testing were used to explore the grafting evidence on the fiber surface, the SEM results show chemical deposition on the wool fiber surface and the scales could not be seen ...
متن کاملFlame-Retardant Cellulosic Fiber Nanocomposite Based on Aluminum Tetraborate and Aluminum Tungstate
متن کامل
Preparation of Flame Retardant Polystyrene via In-Situ Bulk Polymerization Method and Evaluation of its Flammability Properties
In this study, in-situ bulk polymerization was investigated for obtaining flame retardant polystyrene (PS). The halogenated and phosphoric compounds were used as flame retardant additives and Perkadox 30 was used as a synergist. The flammability of the PS was evaluated by thermogravimetric analyzer (TGA), limiting oxygen index (LOI) and UL-94 tests. The results show that polymerization process ...
متن کامل