Influences of Sample Preparation on Nanoindentation Behavior of a Zr-Based Bulk Metallic Glass
نویسندگان
چکیده
Influences of two different sample preparation methods, mechanical polishing and plunge cutting, on nanoindentation behavior of a Zr-based bulk metallic glass were studied. Mechanical polishing suppresses the serrated flow but promotes the creep. In contrast, plunge cutting promotes the serrated flow but suppresses the creep. However, hardness and elastic modulus obtained from these two methods are nearly the same.
منابع مشابه
Microstructure and mechanical properties of electron beam weld joints of a Zr41Ti14Cu12Ni10Be23 bulk metallic glass with Zr
The electron beam welding technique was used to join Zr41Ti14Cu12Ni10Be23 bulk metallic glass (BMG) to crystalline pure Zr. Compositional, microstructural, and mechanical property variations across the welded interface were evaluated. It is shown that a crystalline layer develops close to the welding interface. Transmission electron microscopy of this layer indicates the crystalline phase to be...
متن کاملMicrostructure controlled shear band pattern formation and enhanced plasticity of bulk metallic glasses containing in situ formed ductile phase dendrite dispersions
Results are presented for a ductile metal reinforced bulk metallic glass matrix composite based on glass forming compositions in the Zr-Ti-Cu-Ni-Be system. Primary dendrite growth and solute partitioning in the molten state yields a microstructure consisting of a ductile crystalline Ti-Zr-Nb beta phase, with bcc structure, in a Zr-Ti-Nb-Cu-Ni-Be bulk metallic glass matrix. Under unconstrained m...
متن کاملStudy of the Mechanical Behaviour of a Zr-Based Metallic Glass Rod Using Micro- and Nano-Indentation
The mechanical properties of a Zr55Cu30Al10Ni5 metallic glass rod are investigated by Vickers microhardness and depth-sensing nanoindentation. The alloy exhibits a relatively large hardness which decreases when increasing the maximum applied load. Serrated flow is also observed during nanoindentation. Both effects are related to deformationinduced mechanical softening.
متن کاملFracture Toughness Study on Bulk Metallic Glasses and Novel Joining Method Using Bulk Metallic Glass Solder
The fracture toughness of three new compositional variants of the Zr-Ti-Be-LTM (Late Transition Metal) family of bulk metallic glasses (BMG’s) are studied in the as-cast and annealed condition. Quaternary Zr-Ti-Cu-Be alloys consistently had linear elastic fracture toughness values greater than 80 MPa·m, while Vitreloy 1, a Zr-Ti-Cu-Ni-Be alloy, had an average fracture toughness of 48.5 MPa·m wi...
متن کاملGlass Forming Ability and Corrosion Resistance of Zr-Cu-Ni-Al-Ag Bulk Metallic Glass
Zr70−xCu12.5Ni10Al7.5Agx (x = 0–10) bulk metallic glasses (BMGs) have been prepared by copper mold casting. The glass-forming ability (GFA) and corrosion behavior of Zr-based BMGs have been investigated. It is found that the GFA of Zr-based BMGs first increases and then decreases with the increase of the Ag content, and the best glass former is Zr65Cu12.5Ni10Al7.5Ag5 with the maximum thickness ...
متن کامل