Advanced Flaw Manufacturing and Crack Growth Control
نویسندگان
چکیده
Advanced artificial flaw manufacturing method has become available. The method produces true fatigue cracks, which are representative of most service-induced cracks. These cracks can be used to simulate behaviour of realistic cracks under service conditions. This paper introduces studies of the effects of different thermal loading cycles to crack opening and residual stress state as seen at the surface of the sample and in the ultrasonic signal. In-situ measurements were performed under dynamic thermal fatigue loading of a 20 mm long artificial crack.
منابع مشابه
Damage Assessment using an Inverse Fracture Mechanics approach
This paper studies the application of an inverse methodology for problem solving in fracture mechanics using the finite element analysis. The method was applied to both detection of subsurface cracks and the study of propagating cracks. The procedure for detection of subsurface cracks uses a first order optimization analysis coupled with a penalty function to solve for the unknown geometric par...
متن کاملFatigue Life Prediction Based on Crack Closure and Equivalent Initial Flaw Size
Failure analysis and fatigue life prediction are necessary and critical for engineering structural materials. In this paper, a general methodology is proposed to predict fatigue life of smooth and circular-hole specimens, in which the crack closure model and equivalent initial flaw size (EIFS) concept are employed. Different effects of crack closure on small crack growth region and long crack g...
متن کاملThe Control of Crack Arrays in Thin Films
Thin-film fracture can be used as a nano-fabrication technique but, generally, it is a stochastic process that results in non-uniform patterns. Crack spacings depend on the interaction between intrinsic flaw populations and the fracture mechanics of crack channeling. Geometrical features can be used to trigger cracks at specific locations to generate controlled crack patterns. However, while th...
متن کاملModeling and Crack-growth and Calculate First Intensity Factor with Ansys Software
Study about Fracture Mechanics and the root cause of fracture in order to estimates lifetime for Mechanical parts in designing process and manufacturing have tremendous role in this realm. Stress intensity factor comes into design which not only is dependent to geometry also extremely to load condition; for instance, it is important in failure processes (brittle and ductile Materials) or to pre...
متن کاملStandard Flaws for Eddy Current Probe
Calibration procedures for eddy current inspections often involve the use of artifact standards containing manufactured flaws. The manufactured flaw is assumed to be a good approximation of the type of flaw being sought during the inspection. These manufactured flaws are most often produced by electrical dis charge machining (EDM) , milling, or the controlled growth of fatigue cracks. With simp...
متن کامل