Microstructure Evolution and Mechanical Properties of Al-TiB2/TiC In Situ Aluminum-Based Composites during Accumulative Roll Bonding (ARB) Process
نویسندگان
چکیده
In this study, a kind of Al-TiB₂/TiC in situ composite was successfully prepared using the melt reaction method and the accumulative roll-bonding (ARB) technique. The microstructure evolution of the composites with different deformation treatments was characterized using field emission scanning electron microscopy (FESEM) and a transmission electron microscope (TEM). The mechanical properties of the Al-TiB₂/TiC in situ composite were also studied with tensile and microhardness tests. It was found that the distribution of reinforcement particles becomes more homogenous with an increasing ARB cycle. Meanwhile, the mechanical properties showed great improvement during the ARB process. The ultimate tensile strength (UTS) and microhardness of the composites were increased to 173.1 MPa and 63.3 Hv after two ARB cycles, respectively. Furthermore, the strengthening mechanism of the composite was analyzed based on its fracture morphologies.
منابع مشابه
Effect of the Particle Size on the Deformation and Fracture Behavior of Al/4vol.%Al2O3 Composite Produced by Accumulative Roll Bonding (ARB)
In this study, Al/Al2O3 composites with two different particle sizes of 1 µm and 0.3 µm were produced via accumulative roll bonding (ARB). The microstructure evolution, mechanical properties and fracture behavior of the composites were investigated. Results show that higher ARB cycles are required to achieve a uniform distribution of particles in the composite with 0.3 µm particle size. During ...
متن کاملEffect of Pre-existing Nano Sized Precipitates on Microstructure and Mechanical Property of Al-0.2wt% Sc Highly Deformed by ARB Process
The effect of pre-existing nano sized precipitates on the mechanisms and rate of grain refinement has been investigated during the severe plastic deformation. A binary Al–0.2Sc alloy, containing coherent Al3Sc particles, of 3.62 nm in diameter has been deformed by accumulative roll bonding up to 10 cycles. The resulting deformed structures were quantitatively analyzed using electron backscatter...
متن کاملComputational evaluation of the homogeneity of composites processed by accumulative roll bonding (ARB)
A new computational method based on MATLAB was used to study the effect of different parameters on the homogeneity of composites produced by a severe plastic deformation technique known as accumulative roll bonding. For a higher number of passes, the degree of particle agglomeration and clustering decreased, and an appreciable homogeneity was obtained in both longitudinal and transverse directi...
متن کاملMechanical and Wear Properties of Al-Nip Composites Produced by ARB Process
In this research, Al-Ni particle composite strips are formed by accumulative roll bonding (ARB) process using Al strips and Ni powder. The rule of ARB cycles and volume percentage (Vol%) of Ni powder on the microstructure, wear resistance and mechanical properties of the formed composites are investigated. According to the tensile test results, the yield stress and tensile strengths of the Al -...
متن کاملEffects of reinforcement distribution on the mechanical properties of Al–Fe3O4 nanocomposites fabricated via accumulative roll bonding
This research developed new nanostructured Al–Fe3O4 composites via accumulative roll bonding (ARB). X-ray diffraction (XRD) analysis and field emission scanning electron microscopy were conducted to examine microstructural characteristics and particle distribution in the nanocomposites. Hardness and tensile strength tests were employed to examine their mechanical propertie...