Ammonia Sensing Behaviors of TiO2-PANI/PA6 Composite Nanofibers
نویسندگان
چکیده
Titanium dioxide-polyaniline/polyamide 6 (TiO(2)-PANI/PA6) composite nanofibers were prepared by in situ polymerization of aniline in the presence of PA6 nanofibers and a sputtering-deposition process with a high purity titanium sputtering target. TiO(2)-PANI/PA6 composite nanofibers and PANI/PA6 composite nanofibers were fabricated for ammonia gas sensing. The ammonia sensing behaviors of the sensors were examined at room temperature. All the results indicated that the ammonia sensing property of TiO(2)-PANI/PA6 composite nanofibers was superior to that of PANI/PA6 composite nanofibers. TiO(2)-PANI/PA6 composite nanofibers had good selectivity to ammonia. It was also found that the content of TiO(2) had a great influence on both the morphology and the sensing property of TiO(2)-PANI/PA6 composite nanofibers.
منابع مشابه
Effect of CSA Concentration on the Ammonia Sensing Properties of CSA-Doped PA6/PANI Composite Nanofibers
Camphor sulfonic acid (CSA)-doped polyamide 6/polyaniline (PA6/PANI) composite nanofibers were fabricated using in situ polymerization of aniline under different CSA concentrations (0.02, 0.04, 0.06, 0.08 and 0.10 M) with electrospun PA6 nanofibers as templates. The structural, morphological and ammonia sensing properties of the prepared composite nanofibers were studied using scanning electron...
متن کاملAmmonia gas sensors based on In2O3/PANI hetero-nanofibers operating at room temperature
Indium nitrate/polyvinyl pyrrolidone (In(NO3)3/PVP) composite nanofibers were synthesized via electrospinning, and then hollow structure indium oxide (In2O3) nanofibers were obtained through calcination with PVP as template material. In situ polymerization was used to prepare indium oxide/polyaniline (In2O3/PANI) composite nanofibers with different mass ratios of In2O3 to aniline. The structure...
متن کاملPreparation of a Cu(II)-PVA/PA6 Composite Nanofibrous Membrane for Enzyme Immobilization
PVA/PA6 composite nanofibers were formed by electrospinning. Cu(II)-PVA/PA6 metal chelated nanofibers, prepared by the reaction between PVA/PA6 composite nanofibers and Cu2+ solution, were used as the support for catalase immobilization. The result of the experiments showed that PVA/PA6 composite nanofibers had an excellent chelation capacity for Cu2+ ions, and the structures of nanofibers wer...
متن کاملFabrication of Compound Nanofibers For Antibacterial Applications in Filtration
In the present study, fabrication and characterization of compound composite nanofibers of Polyvinyl Alcohol (PVA) with nano silver and Polyamide 6 (PA6) are demonstrated. Compound composite fibers with core-shell structure were made using co-axial electrospinning method. The shell was made up of nano silver (Ag) impregnated PVA while PA6 was the core material. These compound composite nanofibe...
متن کاملElectrospun Polyaniline Fibers as Highly Sensitive Room Temperature Chemiresistive Sensors for Ammonia and Nitrogen Dioxide Gases
Electrospun polyaniline (PAni) fibers doped with different levels of (+)-camphor-10-sulfonic acid (HCSA) have been fabricated and evaluated as chemiresistive gas sensors. The experimental results, based on both sensitivity and response time, show that doped PAni fibers are excellent ammonia sensors and that undoped PAni fibers are excellent nitrogen dioxide sensors. The fibers exhibit changes i...