Hydrogen Embrittlement Behavior of a 1700 MPa-Class Ultrahigh Strength Steel Containing Hydrogen Traps
نویسندگان
چکیده
Eiji Akiyama , Songjie Li , Yuuji Kimura , Kaneaki Tsuzaki , Nobuyoshi Uno c a National Institute for Materials Science 1-2-1 Sengen, Tsukuba, Ibaraki 305-0047, Japan b School of Materials Science and Engineering, University of Science and Technology Beijing, No. 30 Xueyuan Road, Hidian Zone, Beijing 100083, China c Nippon Steel and Sumikin Metal Products Co, Ltd, SA Bldg., 17-12 Kiba 2-chome, Koto-ku, Tokyo, Japan [email protected]
منابع مشابه
Hydrogen Diffusion and Trapping in Ultrahigh-Strength AerMet 100
AerMet 100 is a new generation ultrahigh-strength steel (UHSS) and is currently specified for manufacturing important aircraft parts such as landing gears. As a UHSS, AerMet 100 is susceptible to internal hydrogen embrittlement (IHE) and the mechanisms are complicated due to the trapping H transport interactions, given the fine-scale microstructural features serving as potential trap sites (dis...
متن کاملHydrogen Embrittlement of High Strength Steel Electroplated with Zinc-cobalt Alloys
Slow strain rate tests were performed on quenched and tempered AISI 4340 steel to measure the extent of hydrogen embrittlement caused by electroplating with zinc-cobalt alloys. The effects of bath composition and pH were studied and compared with results for electrodeposited cadmium and zinc-10%nickel. It was found that Zinc-1%cobalt alloy coatings caused serious hydrogen embrittlement (EI 0.63...
متن کاملA Comparison of Hydrogen Embrittlement and Stress Corrosion Cracking in High Strength Steels
The purpose of this study was to compare the known behavior of hydrogen embrittled high-strength steel to the characteristics of environmentallyinduced stress corrosion failure where hydrogen is continuously generated at the specimen surface. The incubation time for the initiation of slow crack growth was accelerated by prestressing for a fixed time below the lower critical limit. These results...
متن کاملSimplifying Observation of Hydrogen Trapping in Atom Probe Tomography
The presence of hydrogen within the microstructure of an alloy can lead to a serious reduction of ductility known as hydrogen embrittlement. Although the exact mechanisms of this phenomenon are still subject to debate [1], some mitigation strategies are available. Such strategies include minimizing hydrogen ingress with surface coatings, or controlling hydrogen diffusion within via the introduc...
متن کاملCharpy Notch Toughness and Hardness of Reheated Martensite and Lower Bainite
The resistance to hydrogen embrittlement is of essential importance for steels for vessels for storage of hydrocarbons and depends on the effect of absorbed hydrogen on steel ductility. API tests have shown for the 490 MPa yield stress HSLA steels with the microstructure of ferrite and cementite particles a much greater reduction of area than for the 350 MPa steel with the microstructure of pol...