Giant negative thermal expansion in bonded MnCoGe-based compounds with Ni2In-type hexagonal structure.
نویسندگان
چکیده
MnCoGe-based compounds undergo a giant negative thermal expansion (NTE) during the martensitic structural transition from Ni2In-type hexagonal to TiNiSi-type orthorhombic structure. High-resolution neutron diffraction experiments revealed that the expansion of unit cell volume can be as large as ΔV/V ∼ 3.9%. The optimized compositions with concurrent magnetic and structural transitions have been studied for magnetocaloric effect. However, these materials have not been considered as NTE materials partially due to the limited temperature window of phase transition. The as-prepared MnCoGe-based compounds are quite brittle and naturally collapse into powders. By using a few percents (3-4%) of epoxy to bond the powders, we introduced residual stress in the bonded samples and thus realized the broadening of structural transition by utilizing the specific characteristics of lattice softening enforced by the stress. As a result, giant NTE (not only the linear NTE coefficient α but also the operation-temperature window) has been achieved. For example, the average α̅ as much as -51.5 × 10(-6)/K with an operating temperature window as wide as 210 K from 122 to 332 K has been observed in a bonded MnCo0.98Cr0.02Ge compound. Moreover, in the region between 250 and 305 K near room temperature, the α value (-119 × 10(-6)/K) remains nearly independent of temperature. Such an excellent performance exceeds that of most other materials reported previously, suggesting it can potentially be used as a NTE material, particularly for compensating the materials with large positive thermal expansions.
منابع مشابه
Giant barocaloric effect in hexagonal Ni2In-type Mn-Co-Ge-In compounds around room temperature
The most widespread cooling techniques based on gas compression/expansion encounter environmental problems. Thus, tremendous effort has been dedicated to develop alternative cooling technique and search for solid state materials that show large caloric effects. An application of pressure to a material can cause a change in temperature, which is called the barocaloric effect. Here we report the ...
متن کاملCritical dependence of magnetostructural coupling and magnetocaloric effect on particle size in Mn-Fe-Ni-Ge compounds
Magnetostructural coupling, which is the coincidence of crystallographic and magnetic transition, has obtained intense attention for its abundant magnetoresponse effects and promising technological applications, such as solid-state refrigeration, magnetic actuators and sensors. The hexagonal Ni2In-type compounds have attracted much attraction due to the strong magnetostructural coupling and the...
متن کاملTi substitution for Mn in MnCoGe - The magnetism of Mn0.9Ti0.1CoGe
Bulk magnetization measurements (5-320 K; 0-8T) reveal that below room temperature Mn0.9Ti0.1CoGe exhibits two magnetic phase transitions at ~178 K and ~280 K. Neutron diffraction measurements (3-350K) confirm that the transition at ~178K is due to the structural change from the low-temperature orthorhombic TiNiSi-type structure to the higher temperature hexagonal Ni2In-type structure while the...
متن کاملCorrigendum: Giant barocaloric effect in hexagonal Ni2In-type Mn-Co-Ge-In compounds around room temperature
متن کامل
Switching Between Giant Positive and Negative Thermal Expansions of a YFe(CN)6 -based Prussian Blue Analogue Induced by Guest Species.
The control of thermal expansion of solid compounds is intriguing but remains challenging. The effect of guests on the thermal expansion of open-framework structures was investigated. Notably, the presence of guest ions (K+ ) and molecules (H2 O) can substantially switch thermal expansion of YFe(CN)6 from negative (αv =-33.67×10-6 K-1 ) to positive (αv =+42.72×10-6 K-1 )-a range that covers t...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
- Journal of the American Chemical Society
دوره 137 5 شماره
صفحات -
تاریخ انتشار 2015