Subterranean Termite Resistance of Polystyrene-Treated Wood from Three Tropical Wood Species
نویسندگان
چکیده
The objective of this work was to investigate the resistance of three Indonesian wood species to termite attack. Samples from sengon (Falcataria moluccana), mangium (Acacia mangium), and pine (Pinus merkusii) were treated with polystyrene at loading levels of 26.0%, 8.6%, and 7.7%, respectively. Treated and untreated samples were exposed to environmental conditions in the field for 3 months. Untreated specimens of sengon, mangium, and pine had resistance ratings of 3.0, 4.6, and 2.4, respectively, based on a 10-point scale from 0 (no resistance) to 10 (complete or near-complete resistance). Corresponding resistance values of 7.8, 7.2, and 8.2 were determined for specimens treated with polystyrene. Overall weight loss values of 50.3%, 23.3%, and 66.4% were found for untreated sengon, mangium, and pine samples, respectively; for treated samples, the values were 7.6%, 14.4%, and 5.1%, respectively. Based on the findings in this study, overall resistance to termite attack was higher for treated samples compared to untreated samples.
منابع مشابه
Preferences of Coptotermes formosanus Shiraki and Coptotermes gestroi (Wasmann) (Blattodea: Rhinotermitidae) among Three Commercial Wood Species
The Formosan subterranean termite, Coptotermes formosanus Shiraki, and the Asian subterranean termite, Coptotermes gestroi (Wasmann), are both pests of wood in service in Hawaii and Florida. We conducted a laboratory study using method modified from those described in standard E1-09 of the American Wood Protection Association (AWPA 2009) to assess the termite resistance of three commercially av...
متن کاملThe role of particle size of particulate nano-zinc oxide wood preservatives on termite mortality and leach resistance
Historically most residential wood preservatives were aqueous soluble metal formulations, but recently metals ground to submicron size and dispersed in water to give particulate formulations have gained importance. In this study, the specific role nano-zinc oxide (ZnO) particle size and leach resistance plays in termite mortality resulting from exposure to particulate ZnO-treated wood was inves...
متن کاملResponses of Coptotermes formosanus and Reticulitermes flavipes (Isoptera: Rhinotermitidae) to three types of wood rot fungi cultured on different substrates.
This study examined the responses of two termite species, the Formosan subterranean termite, Coptotermes formosanus Shiraki, and the eastern subterranean termite, Reticulitermes flavipes (Kollar), to three types of wood decay fungi: a brown rot fungus, Gloeophyllum trabeum (Persoon: Fries) Murrill; a white rot fungus, Phanerochaete chrysosporium Burdsall; and a litter rot fungus, Marasmiellus t...
متن کاملResistance of Particleboards Made from Fast-Growing Wood Species to Subterranean Termite Attack
Laboratory-made particleboards were tested for their resistance to subterranean termite, Coptotermes curvignathus Holmgren (Order Isoptera, Family Termitidae) by Indonesian standard SNI 01.7207-2006, during four weeks and at the end of the test their mass loss percentage and feeding rate were determined. Particleboards consisted of: jabon (Anthocephalus cadamba, Family Rubiacea) with a density ...
متن کاملUse of a Short Span Field Test to Evaluate Termite Resistance of Eucalyptus Grandis and Bobgunnia Madagascariensis in a Tropical Environment
Despite being treated with preservatives, the service life of transmission poles and fence posts in the Zambian Copperbelt province is close to fifteen years. However, the service life is only two years for untreated timber, mainly due to termite damage. This short service life is exerting more pressure on an already over-burdened timber resource base. This study used an accelerated field test ...
متن کامل