SYNTHESIS AND CHARACTERIZATION OF Al- AND Ti-MCM-41 MATERIALS: APPLICATION TO OXIDATION OF ANTHRACENE
نویسندگان
چکیده
The synthesis and characterization of new molecular sieves of the MCM-41 type are presented in this study. Samples were obtained from the alkoxides of Si, Ti and Al and different long-chain amine and alkylammonium salts surfactants, by the sol-gel method, through moderate agitation at room temperature. The reactions were conducted in two steps, acid hydrolysis (pH=2) and alkaline condensation (pH=10), both taking about 90min. The synthesized crystals were characterized using infrared spectroscopy, thermogravimetry and X-Ray diffraction. Pore diameters and surface areas were measured by N2 adsorption at 77K. Catalytic tests were conducted for anthracene oxidation using different oxidants (H2O2, alkylhydroperoxide) and organic solvents (benzene, tetrahydrofuran).
منابع مشابه
Synthesis of Nanostructure Ti-45Al-5Cr Alloy by Mechanical Alloying and Study the Effect of Cr Addition on Microstructure of TiAl Alloy
In this work, mechanical alloying was employed to produce Ti-50Al and Ti-45Al-5Cr (at%) alloys. Alloying was performed in a planetary mill and the alloying time varying from 5 to 70h. Characterization of the powder mixture was performed by X-ray diffraction (XRD), SEM analyses and DTA test, during mechanical alloying and after annealing at 1100°c in vacuum oven. The results showed, after 50h of...
متن کاملSynthesis and characterization of composite molecular sieves comprising zeolite Beta with MCM-41 structures
Zeolite Beta/MCM-41 composites have been prepared with various crystallinities of zeolite Beta through a twostep crystallization process involving the combination of low crystallinity zeolite Beta synthesis gel with cetyltrimethylammonium bromide surfactant solution. The composites are characterized by XRD, SEM, Si and Al MAS NMR, N2 adsorption, NH3-TPD and catalytic cracking. The experimental ...
متن کاملSYNTHESIS OF FUNCTIONALLY GRADED Al LM25/ZIRCONIA COMPOSITE AND ITS SLIDING WEAR CHARACTERIZATION USING RESPONSE SURFACE METHODOLOGY
Functionally graded aluminium/zirconia metal matrix composite was fabricated using stir casting technique followed by horizontal centrifugal casting process and a hollow cylindrical functionally graded composite (150 x 150 x 16 mm) was obtained with centrifuging speed of 1200 rpm. The microstructural evaluation and hardness test was carried out on the outer and inner surface of the functionally...
متن کاملSynthesis and Characterization of Ti-6Al-6Mo Prepared by Arc Melting Process
The Ti-6Al-6Mo alloy was arc-melted eight times from pure Ti, Al, and Mo. The Ti6Al-6Mo were analyzed by using an optical microscope, SEM-EDS, XRD and Vickers Hardness Tester. Corrosion test was performed by using Hank’s solution at 37 °C and pH 7.4. The optical micrograph showed a similar structure of this alloy. The microstructure of Ti 6Al6Mo was basketweave with lath. The map of Ti, Al an...
متن کاملMagnetic amine-functionalized graphene oxide as a novel and recyclable bifunctional nanocatalyst for solvent-free synthesis of pyrano[3,2-c]pyridine derivatives
The new magnetic amine-functionalized graphene oxide (Fe3O4-GO-NH2) nanocatalyst was prepared through the reaction of 3-aminopropyltriethoxysilane (APTES) with magnetic graphene oxide (Fe3O4-GO). It was characterized by XRD, TEM, SEM, FT-IR and EDX techniques. The intrinsic carboxylic acids on the edges of Fe3O4-GO alo...