An Ex-vivo Shear and tensile bond strengths of orthodontic molar tubes bonded using different techniques

نویسندگان

  • Elham Abu-Alhaija
  • Mohammad Jaradat
  • Ahed Alwahadni
چکیده

BACKGROUND Molar bonding procedures need continuous improvement to be widely accepted clinically and eventually replace molar bands. MATERIAL AND METHODS The purpose of this study was to determine the effects of enamel micro-abrasion and silane coating of the base of molar tubes on shear and tensile bond strengths of orthodontic molar tubes. A total of 200 third molars were randomly allocated into five groups of 40 teeth as follows: group 1: molar tubes bonded to etched teeth (37% phosphoric acid gel; control group); group 2: molar tubes bonded to etched teeth (37% phosphoric acid) with the addition of silane to the base of molar tubes; group 3: molar tubes bonded to teeth pre-treated with 18% hydrochloric acid and pumice (micro-abrasion); group 4: molar tubes bonded to teeth pre-treated with microabrasion with the addition of silane to the base of molar tubes; group 5: molar tubes bonded to teeth pre-treated with microabrasion before conventional acid etching combined with the addition of silane to the base of molar tubes. The bond strength testing was performed using a computer control electromechanical universal testing machine. RESULTS The highest mean shear and tensile bond strengths were recorded in group 5 (13.81±2.54MPa and 13.97±2.29 MPa, respectively). Micro-abrasion alone (group 3) and the combination of enamel micro-abrasion and the addition of silane (group 4) produced bond strength values comparable to the control. CONCLUSIONS Enamel surface pre-treatment (micro abrasion) before conventional acid etching combined with the addition of silane to the base of the molar tube produced the highest bond strengths among all tested groups. Key words:Molar, shear strength, tensile strength, orthodontic appliances.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Effect of Pretreatment with Fluoride, Chlorhexidine, and Mixed Fluoride-Chlorhexidine Gels on Shear Bond Strength of Orthodontic Brackets: An Ex-Vivo Study

Background and Aim: Orthodontic patients are at an increased risk of caries due to difficulty in plaque control. Antimicrobial agents, such as fluoride and chlorhexidine, can be useful in preventing tooth demineralization. The present study aimed to determine the effect of fluoride and chlorhexidine gels and their mixture on the shear bond strength (SBS) of orthodontic brackets. Materials and ...

متن کامل

مقایسه استحکام باند برشی سه نوع سیستم رزینی جهت باند آلیاژ بیس متال به مینای دندان در In vitro

Resin-bonded fixed partial dentures (F.P.D) can be used for conservative treatment of partially edentulous patients. There are numerous studies regarding the strength of resin composite bond to base meta! alloys. Shear bond strength of three resin systems were invistigated. In this study these systems consisted of: Panavia Ex, Mirage FLC and Marathon V. Thirty base metal specimens were prepared...

متن کامل

Effect of Rebonding on the Bond Strength of Orthodontic Tubes: A Comparison of Light Cure Adhesive and Resin-Modified Glass Ionomer Cement In Vitro

The purpose of this study was to determine the impact of different enamel preparation procedures and compare light cure composite (LCC) and resin-modified glass ionomer (RMGI) on the bond strength of orthodontic metal tubes rebonded to the enamel. Twenty human molars were divided into two groups (n = 10). Tubes were bonded using LCC (Transbond XT) in group 1 and RMGI (Fuji Ortho LC) in group 2....

متن کامل

The crystal growth technique--a laboratory evaluation of bond strengths.

An ex vivo study was carried out to determine differences in the bond strengths achieved with brackets placed using a crystal growth technique compared with a conventional acid-etch technique. A solution of 37 per cent phosphoric acid was used for acid-etching and a commercially available polyacrylic acid gel, Crystal-lok for crystal growth. A heavily-filled composite resin was used for all sam...

متن کامل

Comparison of shear bond strength of the stainless steel metallic brackets bonded by three bonding systems

Introduction: In orthodontic treatment, it is essential to establish a satisfactory bond between enamel and bracket. After the self-etch primers (SEPs) were introduced for the facilitation of bracket bonding in comparison to the conventional etch-and-bond system, multiple studies have been carried out on their shear bond strengths which have yielded different results. This study was aimed at co...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 9  شماره 

صفحات  -

تاریخ انتشار 2017