The T6 Heat Treatment of Semi-Solid Metal Processed Alloy A356
نویسندگان
چکیده
A solution treatment of 1 hour at 540 o C provided the best results for rheocast alloy A356-T6. Natural aging has a significant influence on the subsequent artificial aging response of the alloy. Arrhenius-type equations were derived to predict the time-to-peak hardness as a function of artificial aging temperature.
منابع مشابه
Investigation of the T4 and T6 Heat Treatment Cycles of Semi-Solid Processed Aluminium Alloy A356
The heat treatment cycles that are currently applied to semi-solid processed components are mostly those that are in use for dendritic casting alloys. These heat treatments are not necessarily the optimum treatments. It is shown that a decrease of the solution treatment time at 540 o C from 6 hours to 1 hour does not alter the T4 or T6 tensile properties of the SSM processed A356 alloy. Slightl...
متن کاملEffect of Solution Treatment Temperature on Microstructure and Mechanical Properties of A356 Alloy
Over the years, aluminum content in a vehicle part is increasing due to the needs to reduce weight as well as increase fuel efficiency. Most of the cast product in a vehicle part is mostly cast from A356 alloy. It is used because A356 alloy posses’excellent characteristics over other type of alloy such as cast ability, high weight-to-strength ratio, good corrosion resistance and good weld-abili...
متن کاملEFFECTS OF REINFORCEMENT VOLUME FRACTION, REINFORCEMENT SIZE AND SOLUTION HEAT TREATMENT ON THE MICROSTRUCTURE OF THE TWO DIFFERENTLY PROCESSED A35&SICPCOMOSITES
In this study different volume fractions of SiC particles of various sizes were introduced into the semisolid A356 aluminum alloy by a mechanical stirrer. Then the slurry was poured into a permanent die of certain dimensions either when the metal alloy was partially solid (semisolid-semisolid or SS route) or after reheating to above the liquidus temperature of the alloy (semisolid-liquid or SL ...
متن کاملThe Effects of Mould Materials on Microstructure and Mechanical Properties of Cast A356 Alloy
Abstract In this study, the effects of mould materials on microstructure and mechanical properties of cast A356 Al alloy were investigated. The alloy was poured into three different moulds. Then the samples were homogenised and applied T6 heat treatment. The optical, Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) studies were made. Secondary dendrite arm spacing (SD...
متن کاملBreaking through the strength-ductility trade-off dilemma in an Al-Si-based casting alloy
Al-Si-based casting alloys have a great potential in various industrial applications. Common strengthening strategies on these alloys are accompanied inevitably by sacrifice of ductility, known as strength-ductility trade-off dilemma. Here, we report a simple route by combining rapid solidification (RS) with a post-solidification heat treatment (PHT), i.e. a RS + PHT route, to break through thi...
متن کامل