Growth of catalyst-free high-quality ZnO nanowires by thermal evaporation under air ambient
نویسندگان
چکیده
ZnO nanowires have been successfully fabricated on Si substrate by simple thermal evaporation of Zn powder under air ambient without any catalyst. Morphology and structure analyses indicated that ZnO nanowires had high purity and perfect crystallinity. The diameter of ZnO nanowires was 40 to 100 nm, and the length was about several tens of micrometers. The prepared ZnO nanowires exhibited a hexagonal wurtzite crystal structure. The growth of the ZnO nanostructure was explained by the vapor-solid mechanism. The simplicity, low cost and fewer necessary apparatuses of the process would suit the high-throughput fabrication of ZnO nanowires. The ZnO nanowires fabricated on Si substrate are compatible with state-of-the-art semiconductor industry. They are expected to have potential applications in functional nanodevices.
منابع مشابه
Selective Growth of Vertical-aligned ZnO Nanorod Arrays on Si Substrate by Catalyst-free Thermal Evaporation
By thermal evaporation of pure ZnO powders, high-density vertical-aligned ZnO nanorod arrays with diameter ranged in 80–250 nm were successfully synthesized on Si substrates covered with ZnO seed layers. It was revealed that the morphology, orientation, crystal, and optical quality of the ZnO nanorod arrays highly depend on the crystal quality of ZnO seed layers, which was confirmed by the char...
متن کاملSeed/catalyst-free growth of zinc oxide nanostructures on multilayer graphene by thermal evaporation
We report the seed/catalyst-free growth of ZnO on multilayer graphene by thermal evaporation of Zn in the presence of O2 gas. The effects of substrate temperatures were studied. The changes of morphologies were very significant where the grown ZnO structures show three different structures, i.e., nanoclusters, nanorods, and thin films at 600°C, 800°C, and 1,000°C, respectively. High-density ver...
متن کاملA catalyst-free growth of aluminum-doped ZnO nanorods by thermal evaporation
The growth of Al:ZnO nanorods on a silicon substrate using a low-temperature thermal evaporation method is reported. The samples were fabricated within a horizontal quartz tube under controlled supply of O2 gas where Zn and Al powders were previously mixed and heated at 700°C. This allows the reactant vapors to deposit onto the substrate placed vertically above the source materials. Both the un...
متن کاملDirect formation of catalyst-free ZnO nanobridge devices on an etched Si substrate using a thermal evaporation method.
Well-aligned single crystalline ZnO nanobridges have been synthesized selectively across the prefabricated electrodes on silicon substrates by a single-step thermal evaporation method without using any metal catalysts or a predeposited ZnO seed layer that was a prerequisite for such synthesis. The growth region was self-defined by the anisotropic surface of the silicon substrate as initially po...
متن کاملLarge-quantity free-standing ZnO nanowires
Large-quantity ~grams! one-dimensional ZnO nanowires of different sizes have been synthesized by a simple thermal evaporation of ZnO powder in a tube furnace at a temperature controlled to 1000– 1200 °C and pressure to 1–2 Torr air. A mixture of ZnO and graphite powder was used as the source. Fine graphite flakes were used to promote the growth. The graphite flakes are the key for large-quantit...
متن کامل