A carbon nanotube-enhanced SiC coating for the oxidation protection of C/C composite materials
نویسندگان
چکیده
A carbon nanotube-enhanced SiC (CNT-SiC) coating was deposited on C/C composites to improve the oxidation resistance of C/C. The CNT-SiC coating was prepared by direct growth of CNTs on C/C surface at 700oC followed by deposition of SiC using chemical vapor deposition at 1150oC for 1 hour. SiC was deposited on the CNTs as well as the interface between CNTs and C/C, making CNTs strongly rooted on C/C surface. The final CNT-SiC coating consisted of two layers: the CNT-SiC layer and SiC layer. In comparison to the SiC coating, the CNT-SiC coating showed fewer cracks and a better oxidation resistance because the CNTs reduce the stress in the coating caused by the mismatch of the coefficient of thermal expansion between C/C and SiC.
منابع مشابه
Fabrication and inspection of C/Cf-ZrB2-ZrC-SiC and C/Cf-ZrB2-SiC composite parts resistant to ablation by pressureless sintering method
In this research, the aim is to achieve strong and ablation-resistant composite parts C / Cf-ZrB2-ZrC-SiC and C / Cf-ZrB2-SiC by non-pressure sintering method. C / Cf-ZrB2-SiC samples were prepared using synthesized ZrB2 and SiC powders between layers of resin-impregnated carbon fabric. After pressing with pressure 5 times at 1600 وC and heat treatment for 2 hours in a controlled atmosphere fur...
متن کاملOxidation of ZrB2-SiC Composites at 1600 °C: Effect of Carbides, Borides, Silicides, and Chopped Carbon Fiber
The aim of this work is to optimize the oxidation resistance of ZrB2-SiC-based composites with different additives. Effect of nine factors including SiC, Cf, MoSi2, HfB2 and ZrC contents, milling time of Cf (M.t) and SPS parameters such as temperature, time and pressure on oxidation resistance in four levels was investigated. Taguchi design was applied to explore effective parameters for ...
متن کاملA molecular dynamics simulation of water transport through C and SiC nanotubes: Application for desalination
In this work the conduction of ion-water solution through two discrete bundles of armchair carbon and silicon carbide nanotubes, as useful membranes for water desalination, is studied. In order that studies on different types of nanotubes be comparable, the chiral vectors of C and Si-C nanotubes are selected as (7,7) and (5,5), respectively, so that a similar volume of fluid is investigated ...
متن کاملA molecular dynamics simulation of water transport through C and SiC nanotubes: Application for desalination
In this work the conduction of ion-water solution through two discrete bundles of armchair carbon and silicon carbide nanotubes, as useful membranes for water desalination, is studied. In order that studies on different types of nanotubes be comparable, the chiral vectors of C and Si-C nanotubes are selected as (7,7) and (5,5), respectively, so that a similar volume of fluid is investigated ...
متن کاملCo3O4 spinel protection coating for solid oxide fuel cell interconnect application
In the present study, electrophoretic deposition (EPD) method in different electric fields (30 – 300 V / cm) was used to apply Co3O4 spinel coating to SUS 430 as SOFC interconnect. The coated and uncoated specimens were pre-sintered in air at 800 and 900 °C for 3 h followed by cyclic oxidation at 700 and 800 °C for 500 h, respectively. X-ray diffraction analysis (XRD), Scanning Electron Microsc...
متن کامل