Deformation-driven catalysis of nanocrystallization in amorphous Al alloys
نویسندگان
چکیده
Nanocrystals develop in amorphous alloys usually during annealing treatments with growth- or nucleation-controlled mechanisms. An alternative processing route is intense deformation and nanocrystals have been shown to develop in shear bands during the deformation process. Some controversy surrounded the idea of adiabatic heating in shear bands during their genesis, but specific experiments have revealed that the formation of nanocrystals in shear bands has to be related to localized deformation rather than thermal effects. A much less debated issue has been the spatial distribution of deformation in the amorphous alloys during intense deformation. The current work examines the hypothesis that intense deformation affects the regions outside shear bands and even promotes nanocrystal formation in those regions upon annealing. Melt-spun amorphous Al88Y7Fe5 alloy was intensely cold rolled. Microcalorimeter measurements at 60 °C indicated a slight but observable growth of nanocrystals in shear bands over the annealing time of 10 days. When the cold-rolled samples were annealed at 210 °C for one hour, transmission electron images did not show any nanocrystals for as-spun ribbons, but nanocrystals developed outside shear bands for the cold rolled samples. X-ray analysis indicated an increase in intensity of the Al peaks following the 210 °C annealing while the as-spun sample remained "X-ray amorphous". These experimental observations strongly suggest that cold rolling affects regions (i.e., spatial heterogeneities) outside shear bands and stimulates the formation of nanocrystals during annealing treatments at temperatures well below the crystallization temperature of undeformed ribbons.
منابع مشابه
Effect of strain rate on the formation of nanocrystallites in an Al-based amorphous alloy during nanoindentation
The effect of deformation by nanoindentation on nanocrystallization in amorphous Al90Fe5Gd5 was investigated by transmission electron microscopy. Massive precipitation of nanocrystallites is observed within the indents. Under the quasistatic condition used, a temperature rise due to adiabatic heating is likely negligible, confirming that plastic deformation can induce crystallization without a ...
متن کاملEffect of P addition on nanocrystallization and high temperature magnetic properties of low B and Nb containing FeCo nanocomposites
The P content dependencies of the nanocrystallization behaviors and high temperature magnetic properties of the Fe 54.6 Co 29.4 Si 2.8 (B 0.8ÀY P Y) 14 Nb 1 Cu 1 (Y ¼ 0, 0.2, and 0.3) alloys have been investigated. Alloys were prepared by melt spinning and subsequently annealed in an argon atmosphere to induce nanocrystallization. P addition increases primary crystallization temperature (Tx 1),...
متن کاملCrystallization behavior and magnetic properties of Cu-containing Fe–Cr–Mo–Ga–P–C–B alloys
Multicomponent Fe65.5Cr4Mo4Ga4P12C5B5.5 amorphous alloy is known to have good soft magnetic properties combined with large glass-forming ability. Searching for a nanocrystalline structure that could improve its magnetic properties, Cr and Mo were partially substituted by Cu. The devitrification process of Cu-containing alloys shows an additional broad crystallization event that can be described...
متن کاملDeformation-induced nanocrystallization: A comparison of two amorphous Al-based alloys
Using conventional and high-resolution transmission electron microscopy (HRTEM), the effects of rolling at room temperature on the microstructures of amorphous Al90Fe5Gd5 and Al86.8Ni3.7Y9.5 were compared. In rolled Al90Fe5Gd5, nanocrystallites were observed at shear bands, whereas none were observed in rolled Al86.8Ni3.7Y9.5. When HRTEM was combined with with Fourier transform filtering, nanos...
متن کاملNeutron diffraction analysis on FINEMET alloys
Neutron diffraction has been used to study in situ the nanocrystallization process of Fe73.5Cu1Nb3Si22.52xBx (x55, 9, and 12! amorphous alloys. Nanocrystallization results in a decrease of both the silicon content and the grain size of the Fe~Si! phase with increasing value of x. By comparing the radial distribution function peak areas with those predicted for ideal bcc and DO3 structure, it ca...
متن کامل