Block Copolymer Elastomer with Graphite Filler: Effect of Processing Conditions and Silane Coupling Agent on the Composite Properties

نویسندگان

  • Denis Mihaela Panaitescu
  • Raluca Augusta Gabor
  • Cristian Andi Nicolae
  • Anca Constantina Parau
  • Catalin Vitelaru
  • Valentin Raditoiu
  • Mircea Chipara
چکیده

The control of morphology and interface in poly(styrene-ethylene/butylene-styrene) (SEBS) composites with graphitic fillers is extremely important for the design of piezoresistive sensors for body motion or flexible temperature sensors. The effects of a high amount of graphite (G) and silane coupling agent on the morphology and properties of SEBS composites with anisotropic mechanical properties are reported. The physical and chemical bonding of silane to both G and SEBS surface was proved by EDX and TGA results; this improved interface influenced both the thermal and mechanical properties of the composite. The vinyltriethoxysilane (VS) promoted the formation of char residue and, being tightly bound to both SEBS and G, did not show separate decomposition peak in the TGA curve of composites. The mechanical properties were measured on two perpendicular directions and were improved by both the addition of VS and the increased amount of G; however, the increase of storage modulus due to orientation (from 5 to 15 times depending on the composition and direction of the test) was more important than that provided by the increase of G concentration, which was a maximum of four times that obtained for 15 wt % graphite. A mechanism to explain the influence of G content and treatment on the variation of storage modulus and tan δ depending on the direction of the test was also proposed.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Investigation of the Properties of Polyurethane Elastomer Based on Synthesis and Characterization of PTHF-GAP-PTHF Triblock Copolymer

Binder has a key role in the performance of composite propellants. The binders are classified into two neutral and high-energy categories. GAP is one of the most important energetic binders, but it has poor mechanical and thermal properties. The goal of this investigation is to improve the properties of GAP by copolymerizing it with polytetrahydrofuran. New energy triblock copolymer was synthes...

متن کامل

A Novel Method for Fabricating Wearable, Piezoresistive, and Pressure Sensors Based on Modified-Graphite/Polyurethane Composite Films

A wearable, low-cost, highly repeatable piezoresistive sensor was fabricated by the synthesis of modified-graphite and polyurethane (PU) composites and polydimethylsiloxane (PDMS). Graphite sheets functionalized by using a silane coupling agent (KH550) were distributed in PU/N,N-dimethylformamide (DMF) solution, which were then molded to modified-graphite/PU (MG/PU) composite films. Experimenta...

متن کامل

Effects of silane coupling agent amount on mechanical properties and hydrolytic durability of composite resin after hot water storage.

The purpose of this study was to evaluate the effects of the silane coupling agent amount on the flexural properties and hydrolytic durability on an experimental composite resin for understanding the optimum amount of silanation. A spherical filler was silanated with 7 different amounts of gamma-MPTS, 0, 0.17, 0.34, 0.66, 1.36, 2.72 and 5.45 mass%. Photopolymerized experimental composite resins...

متن کامل

Treatment of Inorganic Filler Surface by Silane-Coupling Agent: Investigation of Treatment Condition and Analysis of Bonding State of Reacted Agent

It is well known that enhancing interfacial adhesion between inorganic filler and matrix resin in a composite lead to favorable properties such as excellent mechanical properties, high thermal resistance, prominent electric insulation, low expansion coefficient, and so on. But it should be avoided that much excess of coupling agent is reacted due to a negative impact of their final composite’s ...

متن کامل

Mechanical, Electrical and Electro-Mechanical Properties of Thermoplastic Elastomer Styrene-Butadiene-Styrene/Multiwall Carbon Nanotubes Composites

Composites of styrene-butadiene-styrene (SBS) block copolymer with multiwall carbon nanotubes (MWCNT) were processed by solution casting in order to investigate the influence of filler content, the different ratio of styrene/butadiene in the copolymer and the architecture of the SBS matrix on the electrical, mechanical and electro-mechanical properties of the composites. It was found that fille...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2018