In vitro evaluation of an adhesive monomer as a bonding agent for orthodontic brackets to primary teeth and nickel-chromium ion crowns.
نویسندگان
چکیده
The adhesive monomer, Clearfil New Bond, was used to enhance the bond strength between orthodontic brackets and primary molars, premolars, and NiCr crowns. Twenty specimens of each had this dental adhesive applied according to the manufacturer's instructions in addition to a chemically cured composite material. The remaining specimens (20 each) were bonded without the adhesive monomer. Shear bond strengths were determined using a universal testing machine. Fracture sites were examined to determine the type of bond failure. All bond strengths were significantly increased with the addition of Clearfil New Bond (P < or = 0.0001). The shear bond strength to NiCr crowns with the addition of the adhesive monomer was 7.76 kg. This is comparable to the shear bond strength observed for primary molars (8.66 kg) and premolars (8.65 kg) without adhesive monomer. The observed decrease in adhesive bond failures with the addition of Clearfil New Bond indicated a stronger shear bond strength between the tooth surface and the bracket base. Clearfil New Bond can significantly increase the shear bond strength of orthodontic brackets to both primary molars and premolars. Additionally, it was shown that orthodontic brackets can be successfully bonded to Ni-Cr crowns at strengths comparable to primary or permanent enamel.
منابع مشابه
In vitro Effects of a Neutral Fluoride Agent on Shear Bond Strength and Microleakage of Orthodontic Brackets
Introduction: This study aimed to evaluate the effect of pretreatment with a neutral fluoride agent on shear bond strength (SBS) and microleakage of orthodontic brackets, and to investigate any significant relationship between SBS and microleakage. Methods: Forty intact premolars were selected and randomly divided into 2 groups. Group 1 served as the control, while group 2 underwent treatment w...
متن کاملEvaluation of the Effect of an Experimental Herbal versus Fluoridated Mouthwash on Frictional Resistance and Surface Roughness between Orthodontic Brackets and Two Types of Archwire: In Vitro Study
Introduction: The present study aimed to evaluate an experimental herbal mouthwash, as compared to sodium fluoride mouthwash on the frictional resistance and surface roughness between brackets and two rectangular archwire types. Methods: A total of 60 premolar׳s brackets engaged with 0.019×0.025 archwires made of stainless steel and nickel-titanium alloys were used in this study. The samples we...
متن کاملبررسی آزمایشگاهی میزان ریزنشت براکتهای ارتودنسی باندشده با کامپوزیت بیس متاکریلات و کامپوزیت بیس سایلوران
Background: One of the orthodontic treatment problems, which causes marginal gaps and microleakage between tooth and composite is microleakage of composite bonding of orthodontic brackets. The microleakage formation permitting the passage of bacteria and oral fluids, which may cause white spot lesions under the brackets surface area.This is a clinical problem during orthodontic treatment. Few s...
متن کاملEffect of using a new cyanoacrylate adhesive on the shear bond strength of orthodontic brackets.
During bonding of orthodontic brackets to enamel, conventional adhesive systems use three different agents: an enamel conditioner, a primer solution, and an adhesive resin. A unique characteristic of some new bonding systems is that they need neither a priming agent nor a curing light to bond brackets. Such an approach should be more cost-effective for the clinician and indirectly also for the ...
متن کاملMicroleakage under Orthodontic Metal Brackets Bonded with Three Different Bonding Techniques with/without Thermocycling
Introduction: The aim of this study was to compare the microleakage of beneath the orthodontic brackets bonded with 3 different bonding techniques and evaluate the effect of thermocycling. Methods: One hundred and twenty premolars were randomly divided into 6 groups, received the following treatment: group 1: 37% phosphoric acid gel+Unite primer+Unite adhesive, group 2: 37% phosphoric acid gel+...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Pediatric dentistry
دوره 17 3 شماره
صفحات -
تاریخ انتشار 1995