Surface-initiated polymerization of superhydrophobic polymethylene.

نویسندگان

  • Juan C Tuberquia
  • Nabijan Nizamidin
  • Robert R Harl
  • Jake Albert
  • Jason Hunter
  • Bridget R Rogers
  • G Kane Jennings
چکیده

We report a new surface-initiated polymerization strategy that yields superhydrophobic polymethylene (PM) films from initially smooth substrates of gold and silicon. The films are prepared by assembling a vinyl-terminated self-assembled monolayer, followed by exposure of the surface to a 0.1 M solution of borane, and polymerizing from the borane sites upon exposure to a solution of diazomethane at -17 degrees C. Surface-initiated polymethylenation (SIPM) presents rapid growth in relation to other surface-initiated reactions, producing PM films thicker than 500 nm after 2 min of reaction and 3 microm after 24 h of reaction. AFM and SEM images show the presence of micro- and nanoscale features that enable the entrapment of air when exposed to water. Consistent with this result, these films exhibit advancing water contact angles greater than 160 degrees, dramatically different than 103 degrees measured for smooth PM films, and hysteresis values ranging from 2 degrees to 40 degrees, depending on the substrate and polymerization time. The superhydrophobic character of the films results in the entrapment of air at the polymer/solution interface to provide remarkable resistances greater than 10(10) Omega x cm(2) against the transport of aqueous redox probes and cause the film to behave as a "perfect" capacitor.

برای دانلود رایگان متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Surface initiation from adsorbed polymer clusters: a rapid route to superhydrophobic coatings.

We introduce the use of a hydroborated polyisoprene (PIP) macroinitiator for the rapid surface-initiated growth of superhydrophobic polymethylene (PM) films. Rinsing of a dip-coated PIP film on a methyl-terminated surface atop silicon or gold substrates results in robustly bound, isolated PIP clusters. After hydroboration of the internal olefins, these clusters result in extremely rapid growth ...

متن کامل

Reproducing superhydrophobic leaves as coatings by micromolding surface-initiated polymerization.

Micromolding surface-initiated polymerization enables the fabrication of polymer coatings that reproduce the microscale surface topography of superhydrophobic leaves onto solid supports. Here, the surfaces of superhydrophobic leaves from Trifolium repens and Aristolochia esperanzae are molded and reproduced as the topography of a partially fluorinated polymer coating through the surface-initiat...

متن کامل

Nitroxide-Mediated Radical Polymerization of Styrene Initiated from the Surface of Titanium Oxide Nanoparticles

Titanium dioxide (TiO2) nanoparticles, with an average size of about 45 nm, were encapsulated by polystyrene using in situ nitroxide mediated radical polymerization   in the presence of 3-aminopropyl triethoxy silane (APTES) as a coupling agent and 2, 2, 6, 6-tetramethylpiperidinyl-1-oxy  as a initiator. First, the initiator for NMRP was covalently bonded onto the surface of Titanium dioxide na...

متن کامل

Surface-initiated Atom Transfer Radical Polymerization and Solution Intercalation Methods for Preparation of Cellulose-G-PS-G-PAN/MMT Bionanocomposite

Cellulose was modified by polystyrene (PS) and polyacrylonitrile (PAN) via free radical and living radical polymerization, and then cellulose was used as the matrix in the preparation of polymer/clay nanocomposite, through a solution intercalation method. For this purpose, first, the graft polymerization of styrene (St) onto cellulose fibers was performed by using suspension polymerization and ...

متن کامل

Investigating the superhydrophobic behavior for underwater surfaces using impedance-based methods.

We have investigated the impedance behavior of immersed superhydrophobic (SH) polymethylene surfaces by tailoring the surface tension of the contacting liquid phase to gradually transition the surface from the Cassie to the Wenzel state. Control over the surface tension is accomplished by varying the ethanol content of the aqueous phase. To establish the mechanism of the transition, we imaged t...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

عنوان ژورنال:
  • Journal of the American Chemical Society

دوره 132 16  شماره 

صفحات  -

تاریخ انتشار 2010