Laccase-Catalyzed Surface Modification of Thermo-Mechanical Pulp (TMP) for the Production of Wood Fiber Insulation Boards Using Industrial Process Water

نویسندگان

  • Mark Schubert
  • Pascal Ruedin
  • Chiara Civardi
  • Michael Richter
  • André Hach
  • Herbert Christen
  • Willem J.H. van Berkel
چکیده

Low-density wood fiber insulation boards are traditionally manufactured in a wet process using a closed water circuit (process water). The water of these industrial processes contains natural phenolic extractives, aside from small amounts of admixtures (e.g., binders and paraffin). The suitability of two fungal laccases and one bacterial laccase was determined by biochemical characterization considering stability and substrate spectra. In a series of laboratory scale experiments, the selected commercial laccase from Myceliophtora thermophila was used to catalyze the surface modification of thermo-mechanical pulp (TMP) using process water. The laccase catalyzed the covalent binding of the phenolic compounds of the process water onto the wood fiber surface and led to change of the surface chemistry directly via crosslinking of lignin moieties. Although a complete substitution of the binder was not accomplished by laccase, the combined use of laccase and latex significantly improved the mechanical strength properties of wood fiber boards. The enzymatically-treated TMP showed better interactions with the synthetic binder, as shown by FTIR-analysis. Moreover, the enzyme is extensively stable in the process water and the approach requires no fresh water as well as no cost-intensive mediator. By applying a second-order polynomial model in combination with the genetic algorithm (GA), the required amount of laccase and synthetic latex could be optimized enabling the reduction of the binder by 40%.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Hot-Air/Hot-Steam Process for the Production of Laccase-Mediator-System Bound Wood Fiber Insulation Boards

In this study, a new technical process for hardening wood fiber insulation boards is introduced. During the dry-process, the fibers are usually glued with polymeric-diphenylmethane-diisocyanate (pMDI) and hardened to wood fiber insulation boards using a steam-air mixture. However, the maximum temperature reached in the steam-air process was 100 °C, and it was impossible to use an alternative bi...

متن کامل

Upgradation of Recycled Pulp Using Endoglucanase Enzyme Produced by Pycnoporus sanguineus NFCCI-3628

The importance of recycling and utilization of recycled fiber has recently been recognized because of concerns about environmental issues and economic aspects. In spite of several advantages offered by paper recycling such as wood savings through substitution of virgin pulp and reduction in chemical usage, recycled pulp also contains plenty of fines having high relative surface area and hig...

متن کامل

Thermomechanical Pulp Fiber Surface Modification for Enhancing the Interfacial Adhesion with Polypropylene

Chemical coupling on the thennomechanical pulp (TMF') fiber improved tensile shrength of the TMP fiber handsheet and isotactic polypropylene film laminates (TPL). For the maleic anhydride W) with benzoyl peroxide (%PO) as an initiator, tensile strength i n d 52% with the TMP fiber treatment over untreated laminates. The optimum strength jmperties were obtaiaed with an MA and BPO ratio of 21. Sc...

متن کامل

Fiber reinforced plastic composites using recycled materials

This work investigates the feasibility of using recycled high density polyethylene (rHDPE), recycled polypropylene (rPP) and old newsprint fiber (ONP) to manufacture fiber reinforced composites. The boards were made through air-forming and hot press. The effects of the fiber loading and coupling agent content on tensile, flexural, internal bond properties and water absorption and thickness swel...

متن کامل

Plasma Enhanced Modification of TMP Fiber and its Effect on Tensile Strength of Wood Fiber/PP Composite

Plasma-assisted surface treatment on thermomechanical pulp (TMP) fiber and polypropylene (PP) film was investigated to obtain interfacial adhesion at the wood fiber and PP interface. A metal plate between electrodes prevented thermal damage to the TMP fiber handsheets and PP film. Oxygen-plasma treatment provided better surface activation on the TMP fiber and PP film than argon-plasma treatment...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 10  شماره 

صفحات  -

تاریخ انتشار 2015