Catalytic Effect of Nb2O5 in MgH2-Nb2O5 Ball-Milled Composites
نویسندگان
چکیده
We report a study on the desorption properties, crystallography and chemical state of MgH2 and 1 mol% Nb2O5 ball-milled composites. Desorption temperatures of the composites decreased with increase of ball-milling time. Size of MgH2 crystallites decreased during ball-milling. Reduction of Nb2O5 after ball-milling was confirmed by tracing the chemical state of Nb and was further supported by TEM observation. The reduced phases may act as more effective catalysts improving the desorption properties.
منابع مشابه
Remarkable Improvement of Hydrogen Sorption Kinetics in Magnesium Catalyzed with Nb2O5
Kinetics of hydrogen absorption and desorption reactions was investigated on the MgH2 composite doped with 1 mol% Nb2O5 as a catalyst by ballmilling. The composite after dehydrogenation at 200 °C absorbed gaseous hydrogen of ~ 4.5 mass% even at room temperature under lower pressure than 1 MPa within 15 sec and finally its capacity reached more than 5 mass%. On the other hand, the catalyzed MgH2...
متن کاملElectrochemical Energy Storage Applications of CVD Grown Niobium Oxide Thin Films.
We report here on the controlled synthesis, characterization, and electrochemical properties of different polymorphs of niobium pentoxide grown by CVD of new single-source precursors. Nb2O5 films deposited at different temperatures showed systematic phase evolution from low-temperature tetragonal (TT-Nb2O5, T-Nb2O5) to high temperature monoclinic modifications (H-Nb2O5). Optimization of the pre...
متن کاملDevelopment of AlN and TiB2 Composites with Nb2O5, Y2O3 and ZrO2 as Sintering Aids
The synthesis of AlN and TiB2 by spark plasma sintering (SPS) and the effect of Nb2O5, Y2O3 and ZrO2 additions on the mechanical properties and densification of the produced composites is reported and discussed. After the SPS process, dense AlN and TiB2 composites with Nb2O5, Y2O3 and ZrO2 were successfully prepared. X-ray diffraction analysis showed that in the AlN composites, the addition of ...
متن کاملIn situ synthesized one-dimensional porous Ni@C nanorods as catalysts for hydrogen storage properties of MgH2.
We have demonstrated an extremely facile procedure for the preparation of 1D porous Ni@C nanostructures by pyrolysis of Ni-based coordination polymer nanorods. The highly aligned Ni-based polymer nanorods were prepared using nitrilotriacetic acid (NTA) as a chelating agent by a one-step solvothermal approach. The obtained precursors are demonstrated to have a well-designed 1D nanostructure and ...
متن کاملNb2O5-γ-Al2O3 nanofibers as heterogeneous catalysts for efficient conversion of glucose to 5-hydroxymethylfurfural
One-dimensional γ-Al2O3 nanofibers were modified with Nb2O5 to be used as an efficient heterogeneous catalyst to catalyze biomass into 5-hydroxymethylfurfural (5-HMF). At low Nb2O5 loading, the niobia species were well dispersed on γ-Al2O3 nanofiber through Nb-O-Al bridge bonds. The interaction between Nb2O5 precursor and γ-Al2O3 nanofiber results in the niobia species with strong Lewis acid si...
متن کامل