High Temperature Deformation of Twin-Roll Cast Al-Mn-Based Alloys after Equal Channel Angular Pressing
نویسندگان
چکیده
Twin roll cast Al-Mn- and Al-Mn-Zr-based alloys were subjected to four passes of equal channel angular pressing. The resulting grain size of 400 nm contributes to a significant strengthening at room temperature. This microstructure is not fully stable at elevated temperatures and recrystallization and vast grain growth occur at temperatures between 350 and 450 °C. The onset of these microstructure changes depends on chemical and phase composition. Better stability is observed in the Al-Mn-Zr-based alloy. High temperature tensile tests reveal that equal channel angular pressing results in a softening of all studied materials at high temperatures. This can be explained by an active role of grain boundaries in the deformation process. The maximum values of ductility and strain rate sensitivity parameter m found in the Al-Mn-Zr-based alloy are below the bottom limit of superplasticity (155%, m = 0.25). However, some features typical for superplastic behavior were observed-the strain rate dependence of the parameter m, the strengthening with increasing grain size, and the fracture by diffuse necking. Grain boundary sliding is believed to contribute partially to the overall strain in specimens where the grain size remained in the microcrystalline range.
منابع مشابه
EFFECT OF POST-DEFORMATION ANNEALING TREATMENT ON INTERFACE PROPERTIES AND SHEAR BOND STRENGTH OF Al-Cu BIMETALLIC RODS PRODUCED BY EQUAL CHANNEL ANGULAR PRESSING
Effects of annealing treatment after equal channel angular pressing (ECAP) on the interface properties and shear bond strength of Al/Cu bimetallic rods were investigated. For the as-deformed samples, the one with two passes of ECAP indicated higher shear bond strength. Formation of a layer of intermetallic compounds after annealing treatment is confirmed. In general, by increasing annealing tem...
متن کاملPlastic deformation of 7075 Aluminum Alloy using Integrated Extrusion-Equal Channel Angular Pressing
Grain refinement improves the mechanical properties and formability of metals and alloys. So far, several different grain refinement methods have been proposed and studied. Severe plastic deformation is one of the most promising and efficient methods. Therefore, in the present study the possibility of imposing a two-step severe plastic deformation (Extrusion and Equal channel angular pressing) ...
متن کاملModeling and production of high strength Al strips by equal channel multi angular pressing method
Equal channel multi angular pressing (ECMAP) process is the efficient method to enhance the productivity of ultra-fine grained (UFG) materials, by increasing process continuity and as a result decreasing process required time. Comparing repetitive ECAP method, in the same period, the number of passes can be done by ECMAP. In this article, ECMAP of AL strips in two typical annealed and as receiv...
متن کاملEqual Channel Angular Pressing to Produce Ultrafine Pure Copper with Excellent Electrical and Mechanical Properties
In this article, commercially pure copper samples were severely deformed by equal channel angular pressing (ECAP) up to eight passes at room temperature. The effects of severe plastic deformation on the microstructure, mechanical properties, and electrical conductivity of the copper were investigated. The microstructure evolution was followed by optical microscope and field emission scanning el...
متن کامل3D finite element study of temperature variations during equal channel angular pressing
Equal channel angular pressing is the most promising method of severe plastic deformation with the capability of producing ultrafine grained materials. These materials exhibit improved mechanical and physical properties compared with their coarse grained counter parts.The temperature variation in the sample during ECA-pressing is a key factor determining the final microstructure and mechanical ...
متن کامل