Design, Synthesis and Characterisation of Novel Biodegradable Aliphatic Copolyesters- Poly(ethylene sebacate-co-butylene succinate) and Poly(ethylene sebacate-co-butylene adipate)
نویسنده
چکیده
Synthesis of novel aliphatic biodegradable copolyesters namely Poly (ethylene sebacateco-butylene succinate) and Poly (ethylene sebacate-co-butylene adipate) were carried out using Poly (butylene Succinate), Poly (Butylene Adipate) and Poly (Ethylene Sebacate) in presence of Poly Phosphoric acid. Synthesis of Poly (Butylene Succinate), Poly (Butylene Adipate) and Poly (Ethylene Sebacate) were carried out using respective diols and diacids in presence of titanium tetrabutoxide as catalyst. Newly synthesized copolyesters were characterized by solubility studies, viscosity measurements, thermal analysis, IR Spectroscopy and Nuclear Magnetic Resonance Spectroscopy (1H-NMR and 13C-NMR). The characteristic peaks present in the homopolyesters were recorded in the copolymers as well. DSC analysis of the copolyesters showed multiple melting peaks, while increase of methylene units in the di-acid decreased the Tg.
منابع مشابه
Biodegradation of new series of aliphatic copolyesters by fungi
Biodegradable aliphatic random copolyesters poly(butylene succinate-co-butylene adipate), PBSA and poly(butylene succinate-co-butylene azelate), PBSAz were synthesized from 1,4 butane diol, succinic acid and adipic acid/azelaic acid through direct melt polycondensation with Titanium Tetra isopropoxide (TTiPO) as a catalyst. These polyesters were characterized by Viscosity measurements, 1H NMR s...
متن کاملSynthesis of elastic biodegradable polyesters of ethylene glycol and butylene glycol from sebacic acid.
High molecular weight biodegradable polyesters were prepared from sebacic acid, ethylene glycol and butylene glycol through a simple non-solvent polycondensation with a low toxicity catalyst. The successful synthesis of the polyesters was confirmed by gel permeation chromatography, (1)H-nuclear magnetic resonance and Fourier transform-infrared spectroscopies and differential scanning calorimetr...
متن کاملPerformance of biodegradable microcapsules of poly(butylene succinate), poly(butylene succinate-co-adipate) and poly(butylene terephthalate-co-adipate) as drug encapsulation systems.
Poly(butylene succinate) (PBSu), poly(butylene succinate-co-adipate) (PBSA) and poly(butylene terephthalate-co-adipate) (PBTA) microcapsules were prepared by the double emulsion/solvent evaporation method. The effect of polymer and poly(vinyl alcohol) (PVA) concentration on the microcapsule morphologies, drug encapsulation efficiency (EE) and drug loading (DL) of bovine serum albumin (BSA) and ...
متن کاملWater absorption and degradation characteristics of chitosan-based polyesters and hydroxyapatite composites.
Blends of chitosan and biodegradable synthetic aliphatic polyesters (polycaprolactone, poly(butylene succinate), poly[(butylene succinate)-co-adipate], poly[(butylene terephthalate)-co-adipate], and poly(lactic acid)) were injection-molded. These samples were immersed in isotonic solution at 37 degrees C for a period of 60 d. The water uptake and the degradation properties, as measured by the l...
متن کاملEffect of nanoclay loading on the thermal and mechanical properties of biodegradable polylactide/poly[(butylene succinate)-co-adipate] blend composites.
Polylactide/poly[(butylene succinate)-co-adipate] (PLA/PBSA)-organoclay composites were prepared via melt compounding in a batch mixer. The weight ratio of PLA to PBSA was kept at 70:30, while the weight fraction of the organoclay was varied from 0 to 9%. Small angle X-ray scattering patterns showed slightly better dispersion in PBSA than PLA, and there was a tendency of the silicate layers to ...