Fabrication of porous carbon monoliths with a graphitic framework

نویسندگان

  • Marta Sevilla
  • Antonio B. Fuertes
چکیده

Macro/mesoporous carbon monoliths with a graphitic framework were synthesized by carbonizing polymeric monoliths of poly(benzoxazine-co-resol). The overall synthesis process consists of the following steps: a) the preparation of polymeric monoliths by copolymerization of resorcinol and formaldehyde with a polyamine (tetraethylenepentamine), b) doping the polymer with a metallic salt of Fe, Ni or Co, c) carbonization and d) the removal of inorganic nanoparticles. The metal nanoparticles (Fe, Ni or Co) formed during the carbonization step catalyse the conversion of a fraction of amorphous carbon into graphitic domains. The resulting carbon monoliths contain > 50 wt % of graphitic carbon, which considerably improves their electrical conductivity. The use of tetraethylenepentamine in the synthesis results in a nitrogen-containing framework. Textural characterization of these materials shows that they have a dual porosity made up of macropores and mesopores (~ 2-10 nm), with a BET surface area in the 280-400 m·g range. We tested these materials as electrodes in organic electrolyte supercapacitors and found that no conductive additive is needed due to their high electrical conductivity. In addition, they show a specific capacitance of up to 35 F·g, excellent rate and cycling performance, delivering up to 10 kW kg at high current densities. * Corresponding author. E-mail address: [email protected] (A.B. Fuertes)

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Porous carbon spheres and monoliths: morphology control, pore size tuning and their applications as Li-ion battery anode materials.

The development of the next generation of advanced lithium-ion batteries (LIBs) requires new & advanced materials and novel fabrication techniques in order to push the boundaries of performance and open up new and exciting markets. Structured carbon materials, with controlled pore features on the micron and nanometer scales, are explored as advanced alternatives to conventional graphite as the ...

متن کامل

Structurally designed synthesis of mechanically stable poly(benzoxazine-co-resol)-based porous carbon monoliths and their application as high-performance CO2 capture sorbents.

Porous carbon monoliths with defined multilength scale pore structures, a nitrogen-containing framework, and high mechanical strength were synthesized through a self-assembly of poly(benzoxazine-co-resol) and a carbonization process. Importantly, this synthesis can be easily scaled up to prepare carbon monoliths with identical pore structures. By controlling the reaction conditions, porous carb...

متن کامل

A density functional study on the mechanical properties of metal-free two-dimensional polymer graphitic Carbon-Nitride

Successful synthesis of the stable metal-free two-dimensional polymer graphitic carbon-nitride with remarkable properties has made it as one of the most promising nanostructures in many novel nanodevices, especially photocatalytic ones. Understanding the mechanical properties of nanostructures is of crucial importance. Thus, this study employs density functional theory (DFT) to obtain the mecha...

متن کامل

Ultrahigh Surface Area Three-Dimensional Porous Graphitic Carbon from Conjugated Polymeric Molecular Framework

Porous graphitic carbon is essential for many applications such as energy storage devices, catalysts, and sorbents. However, current graphitic carbons are limited by low conductivity, low surface area, and ineffective pore structure. Here we report a scalable synthesis of porous graphitic carbons using a conjugated polymeric molecular framework as precursor. The multivalent cross-linker and rig...

متن کامل

Synthesis of Porous Carbon Monoliths Using Hard Templates

The preparation of porous carbon monoliths with a defined shape via template-assisted routes is reported. Monoliths made from porous concrete and zeolite were each used as the template. The porous concrete-derived carbon monoliths exhibited high gravimetric specific surface areas up to 2000 m²·g-1. The pore system comprised macro-, meso-, and micropores. These pores were hierarchically arranged...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره   شماره 

صفحات  -

تاریخ انتشار 2014