Preparation and characterization of nanosized P(NIPAM-MBA) hydrogel particles and adsorption of bovine serum albumin on their surface

نویسندگان

  • Xiaoli Zhu
  • Xiangling Gu
  • Lina Zhang
  • Xiang-Zheng Kong
چکیده

Thermosensitive polymer hydrogel particles with size varying from 480 to 620 nm were prepared through precipitation copolymerization of N-isopropylacrylamide with N,N'-methylenebisacrylamide (MBA) in water with ammonium persulfate as the initiator. Only polymer hydrogels without any coagula were obtained when MBA concentration in the monomer mixture was kept between 2.5 and 10.0 wt%; with increased MBA concentration, the monomer conversion was enhanced, the size of the hydrogels was increased, and their shrinking was lessened when heated from 25°C to 40°C. Bovine serum albumin adsorption on the surface of the hydrogels of different MBA content was measured at different pH levels and under different temperatures. The results demonstrated that the adsorption of the protein on the hydrogels could be controlled by adjusting the pH, the temperature of adsorption, and the crosslinking in the hydrogels. The results were interpreted, and the mechanisms of the polymerization were proposed.

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

منابع مشابه

Application of Magnetic Polymer Particles Modified with β–Cyclodextrin for Adsorption of Bovine Serum Albumin

Magnetic polymer particles which were modified by vinyl groups and subjected topolymerization by vinyl β-Cyclodextrin derivative, has been used as adsorbent for sorption andrelease of bovine serum albumin and the equilibrium and kinetics of the adsorption process werestudied. The absorbability and releasing of this protein through the new polymer has beenmeasured by ultraviolet-visible spectros...

متن کامل

Preparation and Characterization of Thermoresponsive Poly(N-isopropylacrylamide-co-acrylic acid)-Grafted Hollow Fe3O4/SiO2 Microspheres with Surface Holes for BSA Release

Thermoresponsive P(NIPAM-AA)/Fe3O4/SiO2 microspheres with surface holes serving as carriers were prepared using p-Fe3O4/SiO2 microspheres with a thermoresponsive copolymer. The p-Fe3O4/SiO2 microspheres was obtained using a modified Pickering method and chemical etching. The surface pore size of p-Fe3O4/SiO2 microspheres was in the range of 18.3 nm~37.2 nm and the cavity size was approximately ...

متن کامل

Preparation and Characterization of Thermoresponsive Poly(N-isopropylacrylamide-co-acrylic acid)-Grafted Hollow Fe₃O₄/SiO₂ Microspheres with Surface Holes for BSA Release.

Thermoresponsive P(NIPAM-AA)/Fe₃O₄/SiO₂ microspheres with surface holes serving as carriers were prepared using p-Fe₃O₄/SiO₂ microspheres with a thermoresponsive copolymer. The p-Fe₃O₄/SiO₂ microspheres was obtained using a modified Pickering method and chemical etching. The surface pore size of p-Fe₃O₄/SiO₂ microspheres was in the range of 18.3 nm~37.2 nm and the cavity size was approximately ...

متن کامل

Adsorption of Bovine Serum Albumin onto Hydroxylapatite: Theoretical Modeling and Measurements

Adsorption of Bovine Serum Albumin (BSA) onto calcium Hydroxyl Apatite (HA), Ca10PO4(OH)2, has been studied by Ultra Violet (UV) spectroscopy. The adsorption isotherms of BSA onto the HA surface at 291.7 K and 303.2 K were satisfactorily presented by Langmuir equation and the evaluated parameters are reported. The specific surface area of H...

متن کامل

Measuring Melittin Uptake into Hydrogel Nanoparticles with Near-Infrared Single Nanoparticle Surface Plasmon Resonance Microscopy

This paper describes how changes in the refractive index of single hydrogel nanoparticles (HNPs) detected with near-infrared surface plasmon resonance microscopy (SPRM) can be used to monitor the uptake of therapeutic compounds for potential drug delivery applications. As a first example, SPRM is used to measure the specific uptake of the bioactive peptide melittin into N-isopropylacrylamide (N...

متن کامل

ذخیره در منابع من


  با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید

برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید

ثبت نام

اگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید

عنوان ژورنال:

دوره 7  شماره 

صفحات  -

تاریخ انتشار 2012