Mechanistic Kinetic Models for Steam Reforming of Concentrated Crude Ethanol on Ni/al2o3 Catalyst
نویسندگان
چکیده
Mechanistic kinetic models were postulated for the catalytic steam reforming of concentrated crude ethanol on a Ni-based commercial catalyst at atmosphere pressure in the temperature range of 673-863 K, and at different catalyst weight to the crude ethanol molar flow rate ratio (in the range 0.9645-9.6451 kg catalyst h/kg mole crude ethanol) in a stainless steel packed bed tubular microreactor. The models were based on Langmuir-Hinshelwood-Hougen-Watson (LHHW) and Eley-Rideal (ER) mechanisms. The optimization routine of Nelder-Mead simplex algorithm was used to estimate the inherent kinetic parameters in the proposed models. The selection of the best kinetic model amongst the rival kinetic models was based on physicochemical, statistical and thermodynamic scrutinies. The rate determining step for the steam reforming of concentrated crude ethanol on Ni/Al2O3 catalyst was found to be surface reaction between chemisorbed CH3O and O when hydrogen and oxygen were adsorbed as monomolecular species on the catalyst surface. Excellent agreement was obtained between the experimental rate of reaction and conversion of crude ethanol, and the simulated results, with ADD% being ±0.46.
منابع مشابه
Methane oxy-steam reforming over a highly efficient Ni/Al2O3 nanocatalyst prepared by microwave-assisted impregnation method
An alumina-supported nickel catalyst was prepared by impregnation of Ni2+ solution onto mesoporous alumina under microwave irradiation (denoted as M-Ni/Al2O3). For comparison, a catalyst with the same nickel content was prepared by conventional impregnation method (denoted as UM-Ni/Al2O3). Both M-Ni/Al2O3 and UM-Ni/Al2O3 catalysts were applied to the syngas (H2 + CO) production by methane oxy-s...
متن کاملOptimization of the preparation procedure of Ni/Al2O3 catalyst for steam reforming of n-butane
Performance of Ni/Al2O3 catalysts (10 wt.% Ni) in steam reforming of n-butane was investigated in terms of n-butane conversion, selectivity to hydrogen and hydrogen yield. The process was carried out in a fixed-bed tubular reactor at 650 °C and atmospheric pressure. The volumetric flow rates of n-butane and steam were 0.1 mL/min and 0.6 mL/min, respectively. The catalysts were prepared by preci...
متن کاملAn Investigation into the Effect of Hydrotalcite Calcination Temperature on the Catalytic Performance of Mesoporous Ni-MgO-Al2O3 Catalyst in the Combined Steam and Dry Reforming of Methane
Several mesoporous nickel-based catalysts with MgO-Al2O3 as the catalyst support were prepared using a co-precipitation method at a constant pH. The supports were prepared from the decomposition of an Mg-Al hydrotalcite-like structure which had already been prepared with Mg/Al=1. Prior to impregnating 10 wt.% nickel on the supports, the precursor was decomposed at several ...
متن کاملSteam reforming of propane over Ni-K/CeO2-Al2O3 catalyst in fluidized- and fixed-bed reactors under low steam to propane ratio
Fluidized bed was employed to investigate propane steam reforming over Ni-K/CeO2-Al2O3 catalyst. The catalyst was characterized by XRD, SEM, TG/DTA, and N2 adsorption-desorption tests. Effects of promoters, space velocity, temperature, and steam/propane (S/C) ratio on propane conversion, H2 yield, H2/CO ratio, and stability were studied and discussed. The experiments were carried out under cond...
متن کاملKinetic comparison of Ni/Al2O3 and Ni/MgO-Al2O3 nano structure catalysts in CO2 reforming of methane
The kinetic characteristics of the Ni/Al2O3 and Ni/MgO-Al2O3 catalysts were investigated in CO2 reforming of methane (CRM). The reaction orders (α and β) and the rate constant (k) were calculated using the non-linear regression analysis, in which the sum of the squared differences of calculated and experimental CO2 reforming of m...