In situ Precursor-Template Route to Semi-Ordered NaNbO3 Nanobelt Arrays
نویسندگان
چکیده
We exploited a precursor-template route to chemically synthesize NaNbO3 nanobelt arrays. Na7(H3O)Nb6O19·14H2O nanobelt precursor was firstly prepared via a hydrothermal synthetic route using Nb foil. The aspect ratio of the precursor is controllable facilely depending on the concentration of NaOH aqueous solution. The precursor was calcined in air to yield single-crystalline monoclinic NaNbO3 nanobelt arrays. The proposed scheme for NaNbO3 nanobelt formation starting from Nb metal may be extended to the chemical fabrication of more niobate arrays.
منابع مشابه
Crystal orientation-ordered ZnS nanobelt quasi-arrays and their enhanced field-emission.
Crystal orientation-ordered ZnS nanobelt quasi-arrays were fabricated using a non-catalytic and template-free thermal evaporation process; field-emission measurements show that these novel arrays are decent field emitters possessing a current density more than 20 times higher than that of randomly-oriented ZnS nanobelt ensembles at a macroscopic field of 5.5 V microm(-1).
متن کاملOrdered Mesostructured CdS Nanowire Arrays with Rectifying Properties
Highly ordered mesoporous CdS nanowire arrays were synthesized by using mesoporous silica as hard template and cadmium xanthate (CdR(2)) as a single precursor. Upon etching silica, mesoporous CdS nanowire arrays were produced with a yield as high as 93 wt%. The nanowire arrays were characterized by XRD, N(2) adsorption, TEM, and SEM. The results show that the CdS products replicated from the me...
متن کاملMorphology-controlled 2D ordered arrays by heating-induced deformation of 2D colloidal monolayer
We develop a strategy to fabricate morphology-controlled two dimensional (2D) ordered arrays by solution-dipping sintered colloidal monolayer template. By heating colloid monolayer templates for different times, the morphology of ordered arrays can be controlled effectively, which is valuable to investigate the morphology-dependent optical, magnetic, electrochemical, catalytic properties of arr...
متن کاملAluminum Nanowire Arrays via Directed Assembly.
Freestanding and vertically-oriented metal nanowire arrays have potential utility in a number of applications, but presently lack a route to fabrication. Template-based techniques, such as electrodeposition into lithographically defined nanopore arrays, have produced well-ordered nanowire arrays with a maximum pitch of about 2 μm; such nanowires, however, tend to cluster due to local attractive...
متن کاملOrdered arrays of tilted silicon nanobelts with enhanced solar hydrogen evolution performance.
Well-ordered tilted silicon nanobelt arrays have been fabricated over a large area (≥2.5 cm(2)) by metal assisted chemical etching of pre-patterned silicon, which demonstrated markedly enhanced solar hydrogen evolution performance, compared with planar silicon of the same type and previously reported silicon nanowires prepared in a similar way.
متن کامل