Effect of a Combined Bleaching Regimen on the Microhardness of a Sealed Methacrylate-based and a Silorane-based Composite

STATEMENT OF PROBLEM The use of tooth bleaching agents has been very popular treatment in dentistry. The bleaching agents have an inherent potential to impair surface properties of existing composite resin restorations. PURPOSE This study evaluated the effect of a combined bleaching regimen on the surface microhardness of a Silorane-based and a sealed methacrylate-based composite. MATERIALS AND METHOD Forty-five specimens of methacrylate-based composite (Ice) and 18 specimens of Silorane composite (Filtek Silorane, 3M ESPE; USA) were prepared and randomly divided into 5 (1-5) and 2 (6-7) groups (n=9), respectively. After 8-week aging, groups 1 and 6 were remained with no treatment. In groups 2, 4 and 5, the specimens were covered by a surface sealant and light cured. In groups 3, 4, 5 and 7, the specimens were bleached with hydrogen peroxide 40% and then carbamide peroxide 20% for seven days. In group 5, after bleaching, the sealant was removed by polishing. Surface microhardness was measured and the data were analyzed using one-way ANOVA and Tukey tests (α=0.05). RESULTS The microhardness values of groups 2 to 4 were significantly lower than that of group1 (p <0.05). There was no significant difference among groups 1, 5, 6 and 7 (p> 0.05). CONCLUSION The combined bleaching regimen used in this study had a substantial negative effect on methacrylate and sealed methacrylate composites but not on Silorane composite. Polishing following the bleaching on the sealed composite yielded a hardness value similar to that of unsealed methacrylate composite (control).