Joint Development of a Fourth Generation Single Crystal Superalloy
نویسنده
چکیده
A new, fourth generation, single crystal superalloy has been jointly developed by GE Aircraft Engines, Pratt & Whitney and NASA. The focus of the effort was to develop a turbine airfoil alloy with long-term durability for use in the High Speed Civil Transport. In order to achieve adequate long-time strength improvements at moderate temperatures and retain good microstructural stability, it was necessary to make significant composition changes from 2 and 3 generation single crystal superalloys. These included lower chromium levels, higher cobalt and rhenium levels and the inclusion of a new alloying element, ruthenium. It was found that higher Co levels were beneficial to reducing both TCP precipitation and SRZ formation. Ruthenium caused the refractory elements to partition more strongly to the γ’ phase, which resulted in better overall alloy stability. The final alloy, EPM-102, had significant creep rupture and fatigue improvements over the baseline production alloys and had acceptable microstructural stability. The alloy is currently being engine tested and evaluated for advanced engine applications.
منابع مشابه
Evaluating the Effect of Ta/W Ratio on Microstructure and Stress Rupture Properties of Ni-Based Single Crystal Superalloy PWA1483
In this study, the effect of Ta/W ratio on the microstructure and stress rupture properties of Ni-based single crystal (SX) superalloy PWA1483 was investigated. For this purpose, single crystal (SX) superalloys with different Ta/W ratios (0.75, 1.0, 1.32 and 1.5 in wt.%) were fabricated. The alloys were directionally solidified by Bridgman method under the same solidification condition at withd...
متن کاملFemtosecond Laser Micromachining of Single-crystal Superalloys
Investigations on femtosecond laser micromachining of single crystal superalloys with and without plasma-sprayed thermal barrier coatings were conducted under laser fluences ranging from 0.1 J/cm up to 160 J/cm. Micromachining was carried out in air using a titanium:sapphire laser system ( = 780 nm) operating at a repetition rate of 1 kHz and delivering individual pulses of ~150 fs duration. Th...
متن کاملInfluence of crystal orientation on the thermomechanical fatigue behaviour in a single- crystal superalloy
متن کامل
ON THE FORMATION OF STRAY GRAINS IN DIRECTIONALLY-SOLIDIFIED NI-BASED SUPERALLOYS WITH VARYING CROSS SECTIONS
Formation of stray grain defects particularly around re-entrant features of the turbine blade airfoils is one of the major problems in directional and single crystal solidification processes. In this work, directional solidification tests of the GTD-111 Ni-based superalloy were conducted at different withdrawal velocities of 3, 6 and 9 mm.min-1 using various stepped cylindrical and cubic design...
متن کاملDetermination of solution temperature in an ex-service Ni-based turbine blade
It is well-known that the harsh operational conditions of turbine blades lead to a gradual change in the microstructure of underlying Ni-based superalloy of blades. According to this, a rejuvenation process should be conducted on turbine blades superalloys to recover their microstructures. The first and main step of rejuvenation process is the determination of appropriate solution condition in ...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
عنوان ژورنال:
دوره شماره
صفحات -
تاریخ انتشار 2005