Synthesis of highly monodisperse porous manganese oxide spheres using a butyric acid microemulsion.
نویسندگان
چکیده
Porous manganese oxide spheres form readily from a reaction between KMnO4 and n-butanol in aqueous butyric acid under ambient conditions. Spheres have uniform size, tuneable diameters and high surface areas. The material is an active catalyst for the oxidation of isopropanol to acetone.
منابع مشابه
Transition-Metal-Doped Manganese Oxide Hollow Nanospheres: Synthesis and Catalytic Activityc
! Manganese oxide hollow spheres with approximate MnO2 stoichiometry were synthesized by aqueous precipitation with a redox reaction between Mn(II) and MnO4– in the presence of butyric acid. The butyric acid acts as a structure-directing agent, reducing the average particle size of the materials, while also acting as a soft template for the spheres to form. This is possible because butyric acid...
متن کاملSynthesis and Investigation the Catalytic Behavior of Cr2O3 Nanoparticles
The use of an inorganic phase in water-in-oil (w/o) microemulsion has recently received considerable attention for preparing metal oxide nanoparticles. This is a technique, which allows preparation of ultrafine metal oxide nanoparticles within the size range 40 to 80 nm. Preparation of nano chromium (III) oxide studied investigated in the inverse microemulsion system. Therefore the nucleation o...
متن کاملNanoscale Hollow Spheres: Microemulsion-Based Synthesis, Structural Characterization and Container-Type Functionality
A wide variety of nanoscale hollow spheres can be obtained via a microemulsion approach. This includes oxides (e.g., ZnO, TiO₂, SnO₂, AlO(OH), La(OH)₃), sulfides (e.g., Cu₂S, CuS) as well as elemental metals (e.g., Ag, Au). All hollow spheres are realized with outer diameters of 10-60 nm, an inner cavity size of 2-30 nm and a wall thickness of 2-15 nm. The microemulsion approach allows modifica...
متن کاملMulti-step Coating of Monodisperse Silica Spheres by Titania Nanoparticles Base on Electrostatic Attraction Strategy
TiO2-SiO2 core-shell particles include of monodisperse silica core and nanostructured titania shell were synthesized by a multi-step coating process. The monodisperse silica spheres were synthesized by Stöber method and titania shell was obtained of a colloidal sol prepared by a hydrolysis–condensation reaction. The titania sol was deposited on monodisperse silica spheres by a multi-step coatin...
متن کاملSynthesis of highly crystalline and monodisperse maghemite nanocrystallites without a size-selection process.
The synthesis of highly crystalline and monodisperse gamma-Fe(2)O(3) nanocrystallites is reported. High-temperature (300 degrees C) aging of iron-oleic acid metal complex, which was prepared by the thermal decomposition of iron pentacarbonyl in the presence of oleic acid at 100 degrees C, was found to generate monodisperse iron nanoparticles. The resulting iron nanoparticles were transformed to...
متن کاملذخیره در منابع من
با ذخیره ی این منبع در منابع من، دسترسی به آن را برای استفاده های بعدی آسان تر کنید
برای دانلود متن کامل این مقاله و بیش از 32 میلیون مقاله دیگر ابتدا ثبت نام کنید
ثبت ناماگر عضو سایت هستید لطفا وارد حساب کاربری خود شوید
ورودعنوان ژورنال:
- Chemical communications
دوره 51 10 شماره
صفحات -
تاریخ انتشار 2015