Atmospheric Plasma Deposition of SiO2 Films for Adhesion Promoting Layers on Titanium
نویسندگان
چکیده
This paper evaluates the deposition of silica layers at atmospheric pressure as a pretreatment for the structural bonding of titanium (Ti6Al4V, Ti15V3Cr3Sn3Al) in comparison to an anodizing process (NaTESi process). The SiO2 film was deposited using the LARGE plasma source, a linearly extended DC arc plasma source and applying hexamethyldisiloxane (HMDSO) as a precursor. The morphology of the surface was analyzed by means of SEM, while the characterization of the chemical composition of deposited plasma layers was done by XPS and FTIR. The long-term durability of bonded samples was evaluated by means of a wedge test in hot/wet condition. The almost stoichiometric SiO2 film features a good long-term stability and a high bonding strength compared to the films produced with the wet-chemical NaTESi process.
منابع مشابه
A Review on Titanium Nitride and Titanium Carbide Single and Multilayer Coatings Deposited by Plasma Assisted Chemical Vapor Deposition
In this paper, we reviewed researches about the titanium nitride (TiN) and titanium carbide (TiC) single and multilayer coatings. These coatings were deposited by the plasma assisted chemical vapor deposition (PACVD) technique. Plasma-based technologies are used for the processing of thin films and coatings for different applications such as automobile and aerospace parts, computer disc drives,...
متن کاملPREPARATION OF CATALYTIC COATING OF TITANIUM OXIDE BY MEANS OF ELECTROLYTIC DEPOSITION
In the current research, the optimum conditions for the electrolytic deposition of TiO2 coatings on titanium pieces were experimentally investigated. Flat pieces of commercially available titanium with dimensions of 50 x20 x3 mm were used as the anode and cathode electrodes. The coatings were applied on the cathode in an electrolyte solution essentially from water and methanol, containing diffe...
متن کاملPulsed laser deposition and characterization of Bi3.25Nd0.75Ti3O12 thin films buffered with La0.7Sr0.3MnO3 electrode
Bi3.25Nd0.75Ti3O12 (BNT) ferroelectric thin films with a thickness of f0.5 Am, on substrates of Pt/Ti/SiO2/Si, (100) SrTiO3 and (100) MgO, with a 0.4-Am-thick La0.7Sr0.3MnO3 (LSMO) layer as bottom electrode, were deposited via pulsed laser deposition. The multilayer thin films were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrical measurement. The LSMO ...
متن کاملStudy of Iridium (Ir) Thin Films Deposited on to SiO2 Substrates
Very smooth thin films of iridium have been deposited on super polished fused silica (SiO2) substrates using dc magnetron sputtering in argon plasma. The influence of deposition process parameters on film micro roughness has been investigated. In addition, film optical constants have been determined using variable angle spectroscopic ellipsometery, over the spectra range from vacuum ultraviolet...
متن کاملCOMPARISON OF PROPERTIES OF TiN/TiCN AND PLASMA NITRIDING/TiCN FILMS DEPOSITED ON THE TOOL STEEL BY PULSED DC- PACVD
In this work, TiN/TiCN & PN/TiCN multilayer films were deposited by plasma- assisted chemical vapour deposition (PACVD). Plasma nitriding (PN) and TiN intermediate layer prior to coating leads to appropriate hardness gradient and it can greatly improve the mechanical properties of the coating. The composition, crystalline structure and phase of the films were investigated by X-ray d...
متن کامل